On the Rehydration of Organic Layered Double Hydroxides to form Low-Ordered Carbon/LDH Nanocomposites

Low-ordered carbon/layered double hydroxide (LDH) nanocomposites were prepared by rehydration of the oxides produced by calcination of an organic LDH. While the memory effect is a widely recognized effect on oxides produced by inorganic LDH, it is unprecedented from the calcination/rehydration of organic ones. Different temperatures (400, 600, and 1100 degrees C) were tested on the basis of thermogravimetric data. Water, instead of a carbonate solution, was used for the rehydration, with CO2 available from water itself and/or air to induce a slower process with an easier and better intercalation of the carbonaceous species. The samples were characterized by X-ray powder diffraction (XRPD), infrared in reflection mode (IR), and Raman spectroscopies and scanning electron microscopy (SEM). XRPD indicated the presence of carbonate LDH, and of residuals of unreacted oxides. IR confirmed that the prevailing anion is carbonate, coming from the water used for the rehydration and/or air. Raman data indicated the presence of low-ordered carbonaceous species moieties and SEM and XRPD the absence of separated bulky graphitic sheets, suggesting an intimate mixing of the low ordered carbonaceous phase with reconstructed LDH. Organic LDH gave better memory effect after calcination at 400 degrees C. Conversely, the carbonaceous species are observed after rehydration of the sample calcined at 600 degrees C with a reduced memory effect, demonstrating the interference of the carbonaceous phase with LDH reconstruction and the bonding with LDH layers to form a low-ordered carbon/LDH nanocomposite.