LOW THERMAL CONDUCTIVE BI-2223 TAPES SHEATHED WITH AG-AU ALLOYS

被引：39

作者：

FUJISHIRO, H ^{[1
]}

IKEBE, M ^{[1
]}

NOTO, K ^{[1
]}

MATSUKAWA, M ^{[1
]}

SASAOKA, T ^{[1
]}

NOMURA, K ^{[1
]}

SATO, J ^{[1
]}

KUMA, S ^{[1
]}

机构：

[1] HITACHI CABLE LTD,ADV RES CTR,TSUCHIURA 300,JAPAN

来源：

IEEE TRANSACTIONS ON MAGNETICS | 1994年 / 30卷 / 04期

关键词：

D O I：

10.1109/20.305574

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

With the view of applying to power current leads for superconducting magnet systems and for other cryogenic power handling systems, low thermal conductive Bi-2223 superconducting tapes sheathed with Ag-Au alloy were fabricated and their thermal conductivities were measured from 12 to 260K. The critical current density (overall-J(c)) was about 1700A/cm2 at 77K, 0T and remained nearly constant irrespective of Au concentration up to 11 at.%. The tape sheathed with Ag + 11 at.% Au alloy, of which the superconductor cross-section ratio f(sc) was 0.65, had a thermal conductivity value about 0.2W/cmK at 77K. This value is as low as that of Cu-Zn. It was found that the thermal conductivity of the tape was close to the calculated one based on f(sc) and the independently measured thermal conductivities, of the Ag-Au alloy and the Bi-2223 superconductor.The superconducting tapes sheathed with the alloy were confirmed to be suitable for the application as power current leads.

引用

页码：1645 / 1650

页数：6

共 12 条

[1] THERMOELECTRIC POWER AND THERMAL CONDUCTIVITY IN SILVER-GOLD ALLOY SYSTEM FROM 3-300 DEGREES K [J].

CRISP, RS ;

RUNGIS, J .

PHILOSOPHICAL MAGAZINE, 1970, 22 (176) :217-&

[2]

FUJISHIRO H, IN PRESS CRYOGENICS

[3]

FUJISHIRO H, 1993, CRYO ENG, V28, P533

[4]

GUBSER DU, 1990, J SUPERCOND, V3, P222

[5] EUROPEAN PROJECT FOR THE DEVELOPMENT OF HIGH T-c CURRENT LEADS [J].

Herrmann, P. F. ;

Albrecht, C. ;

Bock, J. ;

Cottevieille, C. ;

Elschner, S. ;

Herkert, W. ;

Lafon, M-O ;

Lauvray, H. ;

Leriche, A. ;

Nick, W. ;

Preisler, E. ;

Salzburger, H. ;

Tourre, J-M. ;

Verhaege, T. .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1993, 3 (01) :876-880

[6] ANALYSIS OF SELF-COOLED BINARY CURRENT LEADS CONTAINING HIGH-TEMPERATURE SUPERCONDUCTORS [J].

HULL, JR ;

UNAL, A ;

CHYU, MC .

CRYOGENICS, 1992, 32 (09) :822-828

[7]

NOMURA K, IN PRESS APPL PHYS L

[8] EFFECT OF MAGNETIC-FIELD ON THERMAL-CONDUCTIVITY OF YBA2CU3O7-DELTA SINGLE-CRYSTALS [J].

PEACOR, SD ;

COHN, JL ;

UHER, C .

PHYSICAL REVIEW B, 1991, 43 (10) :8721-8724

[9]

SASAOKA T, UNPUB CHARACTERISTIC

[10] TRANSPORT CURRENT PROPERTIES OF SILVER-SHEATHED BIPBSRCACUO WIRE AND COIL [J].

SATO, K ;

HIKATA, T ;

UEYAMA, M ;

MUKAI, H ;

SHIBUTA, N ;

KATO, T ;

MASUDA, T .

CRYOGENICS, 1991, 31 (07) :687-689

← 1 2 →