DTA, DENSITY AND INFRARED-SPECTRA STUDIES OF THE STRUCTURE OF VANADIUM PHOSPHATE-GLASSES CONTAINING LITHIUM-OXIDE

被引:0
作者
FAROUK, H
ELDIN, FME
FARHAN, H
ELBATAL, HA
KASHIF, I
机构
来源
PHYSICS AND CHEMISTRY OF GLASSES | 1994年 / 35卷 / 05期
关键词
D O I
暂无
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The effect of replacing V2O5 by Li2O in vanadium phosphate glass samples was studied. Both infrared absorption spectra and differential thermal analysis, in addition to density measurements were performed. It was found that the number of oxygens increase in the network, also the vanadium ions are present in network forming positions, while lithium ions take only the interstitial positions. The transition temperature T-g and density were found to decrease with increasing Li2O content up to 15 mol% and then increase. The decrease was assumed to be related to the decrease in the mean crosslink densities, the increase of the number of nonbridging oxygens and mean bond strength. The final increase may be attributed to the increase in the packing density of the structure.
引用
收藏
页码:207 / 209
页数:3
相关论文
共 20 条
[1]   OPTICAL ABSORPTION PROPERTIES OF VANADATE GLASSES [J].
ANDERSON, GW ;
COMPTON, WD .
JOURNAL OF CHEMICAL PHYSICS, 1970, 52 (12) :6166-&
[2]  
Bachmann H. G., 1961, Z KRISTALLOGR, V115, P110, DOI DOI 10.1524/ZKRI.1961.115.1-2.110
[3]   VIBRATIONAL-SPECTRUM OF SR2V2O7 AND VIBRATIONAL PROPERTIES OF DIVANADATE ION [J].
BARAN, EJ ;
BOTTO, IL ;
PEDREGOSA, JC ;
AYMONINO, PJ .
MONATSHEFTE FUR CHEMIE, 1978, 109 (01) :41-51
[4]  
BARAN EJ, 1978, MH CHEM, V109, P1114
[5]  
BHORGAVA BN, 1977, APPL SPECTROSC, V31, P23
[6]  
Bray P. J., 1967, INTERACTION RAD SOLI
[7]   THERMAL, PHYSICAL, ELECTRICAL AND XPS STUDIES OF THE LI2O-P2O5-MOO3 GLASS SYSTEM [J].
CHOWDARI, BVR ;
TAN, KL ;
CHIA, WT ;
GOPALAKRISHNAN, R .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1991, 128 (01) :18-29
[8]   ELECTRICAL-PROPERTIES OF BINARY SEMICONDUCTING OXIDE GLASSES CONTAINING 55 MOLE-PERCENT V2O5 [J].
CHUNG, CH ;
MACKENZIE, JD .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1980, 42 (1-3) :357-370
[9]   MIXED IONIC ELECTRONIC CONDUCTION IN SODIUM-BORATE GLASSES WITH LOW V2O5 CONTENT [J].
DOWEIDAR, H ;
MEGAHED, A ;
GOHAR, IA .
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 1986, 19 (10) :1939-1946
[10]   DENSITIES OF V2O5/P2O5 GLASSES AND OXYGEN MOLAR VOLUME [J].
DRAKE, CF ;
STEPHAN, JA ;
YATES, B .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1978, 28 (01) :61-65