STUDIES ON LOW RARE-EARTH ND-FE-B COMPOSITIONS

被引：20

作者：

PANCHANATHAN, V

机构：

[1] MAGNEQUENCH, Delphi Energy & Engine Management Systems, General Motors Corporation, Anderson

来源：

IEEE TRANSACTIONS ON MAGNETICS | 1995年 / 31卷 / 06期

关键词：

Permanent magnets;

D O I：

10.1109/20.489583

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Investigations have been carried out to evaluate the optimum Nd-Fe-B composition to have H-ci of at least 4 kOe. The otpimum composition for the best magnetic properties is as follows: TRE 18 wt. %, B 1 wt. % and balance Fe. The magnetic I,roperties are B-r, 10.1 kG, H-ci 4.3 kOe and BHmax 12.5 MGOe. All the additives (Ga, Nb, Mo, V, Cr) with or without cobalt addition did not improve the magnet properties. The bonded magnets made using this material had B-r value slightly higher than the standard MQP-B powder. The low coercivity of these materials limit their operating temperature to 80 degrees C. This material having Nd2Fe14B/proportional to-Fe structure shows improved saturation behavior compared to those having Nd2Fe14B/Fe3B and Nd2Fe14B structures. It would then be a good candidate for applications where magnetization is difficult.

引用

页码：3605 / 3607

页数：3

共 50 条

[21] Solidification behavior in undercooled Nd-Fe-B alloys [J].

Ozawa, S ;

Saito, T ;

Yu, J ;

Motegi, T .

JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 322 (1-2) :276-280

[22] Phase Equilibria of the Nd-Fe-B Ternary System [J].

G. Fu ;

J. Wang ;

M. H. Rong ;

G. H. Rao ;

H. Y. Zhou .

Journal of Phase Equilibria and Diffusion, 2016, 37 :308-318

[23] Corrosion Behavior of Sintered Nd-Fe-B Magnets [J].

Li Hongying ;

Hao Zhuangzhi ;

Liu Yuhui ;

Zhu Wangwei ;

Chen Yunzhi ;

Duan Junying .

RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (05) :1451-1458

[24] Electron holography of Nd-Fe-B nanocomposite magnets [J].

Shindo, D ;

Park, YG ;

Murakami, Y ;

Gao, Y ;

Kanekiyo, H ;

Hirosawa, S .

SCRIPTA MATERIALIA, 2003, 48 (07) :851-856

[25] Thermodynamic description of the Nd-Fe-B ternary system [J].

Chen, T. L. ;

Wang, J. ;

Guo, C. P. ;

Li, C. R. ;

Du, Z. M. ;

Rao, G. H. ;

Zhou, H. Y. .

CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2019, 66

[26] Anisotropic exchange in Nd-Fe-B permanent magnets [J].

Gong, Qihua ;

Yi, Min ;

Evans, Richard F. L. ;

Gutfleisch, Oliver ;

Xu, Bai-Xiang .

MATERIALS RESEARCH LETTERS, 2020, 8 (03) :89-96

[27] Improvement of coercivity in Nd-Fe-B nanocomposite magnets [J].

Saito, Tetsuji ;

Nozaki, Shunji ;

Nishio-Hamane, Daisuke .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2018, 445 :49-52

[28] Phase Equilibria of the Nd-Fe-B Ternary System [J].

Fu, G. ;

Wang, J. ;

Rong, M. H. ;

Rao, G. H. ;

Zhou, H. Y. .

JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2016, 37 (03) :308-318

[29] Features of magnetization behavior in the rare-earth intermetallic compound (Nd0.5Ho0.5)2Fe14B [J].

Kostyuchenko, N. V. ;

Tereshina, I. S. ;

Gorbunov, D. I. ;

Tereshina-Chitrova, E. A. ;

Andreev, A. V. ;

Doerr, M. ;

Politova, G. A. ;

Zvezdin, A. K. .

INTERMETALLICS, 2018, 98 :139-142

[30] Fabrication of low-cost Nd-Fe-B sintered magnets reusing ultrafine powders [J].

Cui, X. G. ;

Yan, M. ;

Ma, T. Y. ;

Luo, W. ;

Tu, S. J. .

MATERIALS SCIENCE AND TECHNOLOGY, 2010, 26 (02) :193-196

← 1 2 3 4 5 →