FATIGUE BEHAVIOR OF NOZZLE CORNER CRACKS

被引:1
|
作者
CHAI, GZ [1 ]
HONG, QC [1 ]
LI, ZZ [1 ]
机构
[1] GEN MACHINERY INST,HEFEI,PEOPLES R CHINA
关键词
Pressure Vessels;
D O I
10.1016/0013-7944(90)90388-W
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
In the present paper, the fatigue propagation of nozzle corner cracks is experimentally researched through nine pieces of plate-nozzle models and a large pressure vessel (D = 1000 × 4500 mm) with five nozzles. The experimental results show that the fatigue propagation rate of nozzle corner cracks in both plate-nozzle models and the P.V. is well consistent with one of standard specimen and accords excellently with Paris formula when the stress intensity factor of nozzle corner crack by the authors (Hong Qichao and Chai Guozhong, 5th Nat. Symp. in Fracture Mech. China 487-492, May 1988) is used. © 1990.
引用
收藏
页码:661 / 666
页数:6
相关论文
共 50 条
  • [21] DESCRIPTION OF BEHAVIOR OF SHORT FATIGUE CRACKS
    SAEHN, S
    SCHAPER, M
    SAELIGER, P
    SOVIET MATERIALS SCIENCE, 1989, 25 (05): : 456 - 459
  • [22] Prediction of the behavior of small fatigue cracks
    Endo, M.
    McEvily, A. J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 468 : 51 - 58
  • [23] Engineering critical assessment of RPV with nozzle corner cracks under pressurized thermal shocks
    Li, Yuebing
    Jin, Ting
    Wang, Zihang
    Wang, Dasheng
    NUCLEAR ENGINEERING AND TECHNOLOGY, 2020, 52 (11) : 2638 - 2651
  • [24] FATIGUE CRACK-GROWTH IN REINFORCED PANELS WITH INITIAL CORNER CRACKS
    BRUSSAT, TR
    CHIU, ST
    RUDD, JL
    CREAGER, M
    ENGINEERING FRACTURE MECHANICS, 1981, 14 (04) : 665 - 683
  • [25] AN EXPERIMENTAL-TECHNIQUE TO STUDY THE BEHAVIOR OF SMALL CORNER CRACKS
    CRAIG, D
    KUJAWSKI, D
    ELLYIN, F
    INTERNATIONAL JOURNAL OF FATIGUE, 1995, 17 (04) : 253 - 259
  • [26] PWR NOZZLE 'CROTCH CORNER' INSPECTION: AN EFFECTIVE ADDITIONAL ULTRASONIC TECHNIQUE FOR RADIAL CRACKS.
    Coffey, J.M.
    Wrigley, J.M.
    British Journal of Non-Destructive Testing, 1983, 25 (03): : 130 - 131
  • [27] Influence of interaction among multiple cracks on crack propagation in nozzle corner of reactor pressure vessel
    Cheng, Yanting
    Huang, Mei
    Li, Yaodi
    Liu, Weiyang
    Wang, Boxue
    Meng, Xiangyuan
    Ouyang, Xiaoping
    ANNALS OF NUCLEAR ENERGY, 2023, 194
  • [28] APPROXIMATE EXPRESSION OF THE MAXIMUM VALUE OF THE STRESS INTENSITY FACTOR (SIF) OF OBLIQUE NOZZLE CORNER CRACKS
    CAI, ST
    WANG, RJ
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1990, 42 (03) : 353 - 361
  • [29] GROWTH-BEHAVIOR OF SMALL FATIGUE CRACKS
    ZHOU, JG
    ZHONG, JY
    FENG, ZX
    LI, N
    INTERNATIONAL JOURNAL OF FATIGUE, 1993, 15 (02) : 141 - 144
  • [30] Fatigue behavior of internal and surface cracks in vacuum
    Kujawski, D.
    Vasudevan, A. K.
    Sadananda, K.
    ENGINEERING FRACTURE MECHANICS, 2022, 269