EFFECT OF MECHANICAL TREATMENT ON THE REACTIVITY OF AMMONIUM-PERCHLORATE

Thermal reactivities of ammonium perchlorate (AP) pressed at 1500 kg cm** minus **2 for various dwell times ranging from 0 to 45 min have been investigated. Reactivity of AP is obseved to (a) increase with increase of dwell time up to 15 min and (b) decrease for the compacts obtained at higher dewll times. X-ray diffraction profiles of the compacts indicated a broadening up to 15 min dwell time and a narrowing thereafter. The increase in the reactivity has been attributed to the increase in the number of gross imperfections and plastic deformation of particles. The decrease in the reactivity is explained in terms of recrystallization after plastic deformation. Local heating is shown to exist during compaction though its macroscopic effect is insignificant during compaction of AP.