RELATIONSHIPS BETWEEN FRACTURE PARAMETERS AND FRACTURE SURFACE-ROUGHNESS OF BRITTLE POLYMERS

被引：93

作者：

ARAKAWA, K

TAKAHASHI, K

机构：

[1] Research Institute for Applied Mechanics, Kyushu University, Kasuga-shi

来源：

INTERNATIONAL JOURNAL OF FRACTURE | 1991年 / 48卷 / 02期

关键词：

D O I：

10.1007/BF00018393

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Fracture parameters such as crack velocity a, stress intensity factor K(d) and a specific crack extension resistance R* were measured for Homalite-100, PMMA and epoxy in the course of fast crack propagation using a Cranz-Schardin type high speed camera. Fracture surface roughness lambda was evaluated as a function of crack length a so that it could be correlated with the fracture parameters above. The results showed that none of those parameters could be uniquely related to lambda. Instead, there was a good correlation between lambda and a product R* a.

引用

页码：103 / 114

页数：12

共 20 条

[1] ARAKAWA K, 1988, 6TH P INT C EXP MECH, V2, P746
[2] COTTEREL.B, 1968, INT J FRACT MECH, V4, P209
[3] COTTERELL B, 1965, APPL MATER RES, P227
[4] CRAGGS JW, 1962, FRACTURE SOLIDS, P51
[5] APPLICATION OF A DYNAMIC NUMERICAL-SOLUTION TO HIGH-SPEED FRACTURE EXPERIMENTS .2. RESULTS AND A THERMAL BLUNTING MODEL
CROUCH, BA
WILLIAMS, JG
[J]. ENGINEERING FRACTURE MECHANICS, 1987, 26 (04) : 553 - 566
[6] Eshelby J.D., 1970, INELASTIC BEHAV SOLI, P77
[7] ON SHAPE AND SIZE OF FRACTURE ZONES ON GLASS FRACTURE SURFACES
JOHNSON, JW
HOLLOWAY, DG
[J]. PHILOSOPHICAL MAGAZINE, 1966, 14 (130): : 731 - &
[8] KALTHOFF JF, 1983, FEB WORKSH DYN FRACT, P11
[9] KOBAYASHI T, 1978, EXPT MECHANICS, V18, P11
[10] Kobayashi T., 1977, ASTM SPEC TECH PUBL, V627, P257

← 1 2 →