SYNTHESIS AND CHARACTERIZATION OF URETHANE - METHACRYLATES .1.

被引：0
作者：
VARMA, IK
KRISHNAN, PSG
CHOUDHARY, V
机构：
来源：
JOURNAL OF THERMAL ANALYSIS | 1990年 / 36卷 / 7-8期
关键词：
D O I：
暂无
中图分类号：
O414.1 [热力学];
学科分类号：
摘要：
The paper describes the synthesis of urethane methacrylate resins by reaction of tolylene diisocyanate (TDI), butanol-1 (B) and 2-hydroxyethylmethacrylate (HEMA) by a two step procedure. Characterisation was done using FT-IR, FT-NMR, Mass Spectroscopy. The effect of temperature on the UV-curing behaviour was investigated by differential photocalorimetry. An activation energy of 8.4 kJ/mole was found in the temperature range of 50-100-degrees-C. Free radical polymerisation in presence of benzoyl peroxide was also investigated. The polymers were stable upto 200-degrees-C in N2 atmosphere. A two step decomposition was observed in the temperature range of 200-500-degrees-C.
引用
收藏
页码：2611 / 2622
页数：12
相关论文
共 7 条
[1]   RECENT ADVANCES IN ISOCYANATE CHEMISTRY [J].
ARNOLD, RG ;
NELSON, JA ;
VERBANC, JJ .
CHEMICAL REVIEWS, 1957, 57 (01) :47-76
[2]   PROPERTIES OF UV CURABLE POLYURETHANE ACRYLATES [J].
KOSHIBA, M ;
HWANG, KKS ;
FOLEY, SK ;
YARUSSO, DJ ;
COOPER, SL .
JOURNAL OF MATERIALS SCIENCE, 1982, 17 (05) :1447-1458
[3]  
KUSHNER L, 1983, MOD PLAST, V60, P87
[4]   EFFECTS OF COMPOSITION AND POLYMERIZATION MECHANISM ON THE MECHANICAL-PROPERTIES OF UV-CURED CROSSLINKED POLYMERS [J].
LEVY, N ;
MASSEY, PE .
POLYMER ENGINEERING AND SCIENCE, 1981, 21 (07) :406-414
[5]   SYNTHESIS AND CHARACTERIZATION OF RADIATION CURABLE POLYURETHANES CONTAINING PENDANT ACRYLATE GROUPS [J].
LI, C ;
NAGARAJAN, RM ;
CHIANG, CC ;
COOPER, SL .
POLYMER ENGINEERING AND SCIENCE, 1986, 26 (20) :1442-1450
[6]   PROPERTIES OF UV-CURED POLYURETHANE ACRYLATES: EFFECT OF POLYOL TYPE AND MOLECULAR WEIGHT [J].
Lin, Shaow B. ;
Tsay, S. Y. ;
Speckhard, T. A. ;
Hwang, K. K. S. ;
Jezerc, J. J. ;
Cooper, S. L. .
CHEMICAL ENGINEERING COMMUNICATIONS, 1984, 30 (3-5) :251-273
[7]   PROPERTIES OF UV-CURABLE POLYURETHANE ACRYLATES - EFFECT OF REACTIVE DILUENT [J].
SPECKHARD, TA ;
HWANG, KKS ;
LIN, SB ;
TSAY, SY ;
KOSHIBA, M ;
DING, YS ;
COOPER, SL .
JOURNAL OF APPLIED POLYMER SCIENCE, 1985, 30 (02) :647-666
1