HARDNESS OF IRRADIATED AND HELIUM IMPLANTED DIN-1.4914 MARTENSITIC STAINLESS-STEEL

被引：6
|
作者：
CHEN, JC
JUNG, P
机构：
[1] Association Euratom -KFA, Institut für Festkörperforschung, Forschungszentrum Jülich
来源：
JOURNAL OF NUCLEAR MATERIALS | 1994年 / 212卷 / pt A期
关键词：
D O I：
10.1016/0022-3115(94)90122-8
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microhardness of DIN 1.4914 (MANET) martensitic stainless steel, irradiated and helium implanted at room temperature, was measured at temperatures from -180 degrees C to +160 degrees C. Measurements were also performed after annealing at 450 and 650 degrees C and on specimens which were implanted at 600 degrees C and irradiated at 520 degrees C. The results are discussed in terms of the effect of transmutant helium and displacement damage on the ductile to brittle transition temperature.