RAPID SOLIDIFICATION OF AL-CR-ZR-MN ALLOYS

被引：11
|
作者：
ADKINS, NJE [1 ]
TSAKIROPOULOS, P [1 ]
机构：
[1] UNIV SURREY,DEPT MAT SCI & ENGN,GUILDFORD GU2 5XH,SURREY,ENGLAND
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1991年 / 134卷
关键词：
D O I：
10.1016/0921-5093(91)90945-J
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The suppression of the Al11Cr2 and Al13Cr2 intermetallics in A15.1Cr-1.4Zr-1.5Mn (alloy A) and Al-3.3Cr-0.7Zr-0.7Mn (alloy B) has been studied by chill casting in cylindrical and wedge-shaped moulds. In alloy A the former phase is suppressed at approximately 500 K s-1 and the latter at approximately 10(4) K s-1. In alloy B the alpha-Al cellular structure free of the Al13Cr2 intermetallics is formed at cooling rates of 5 x 10(2) K s-1 to 2 x 10(3) K s-1 and shows an age hardening response reaching the peak hardness of 1500 MPa after 25 h at 400-degrees-C. The solid solution strengthening contribution of chromium, zirconium and manganese in alloy B is 536 MPa and the precipitate contribution of the metastable Ll2 Al3Zr phase at the peak aged condition is 571 MPa.
引用
收藏
页码：1158 / 1161
页数：4
相关论文
共 50 条
  • [41] Influence of Cr on Weld Solidification Cracking in Fe-15Mn-0.5C-3.5Al-xCr Alloys
    Yoo, Jaehong
    Kim, Bongyoon
    Jeong, Yoodam
    Park, Younghwan
    Lee, Changhee
    ISIJ INTERNATIONAL, 2015, 55 (01) : 257 - 263
  • [42] Influence of Yb on the Phase Composition and Mechanical Properties of Low-Scandium Al–Mg–Mn–Zr–Sc and Al–Mg–Cr–Zr–Sc Alloys
    A. V. Pozdnyakov
    R. Yu. Barkov
    V. S. Levchenko
    Physics of Metals and Metallography, 2020, 121 : 84 - 88
  • [43] DIRECTIONAL SOLIDIFICATION AND ANNEALING OF MN55AL45 ALLOYS
    PIRICH, RG
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (07): : 1247 - 1249
  • [44] Al-Cr-Zr alloys for high temperature applications
    Gerique, T
    Brahmi, A
    Lieblich, M
    Torralba, M
    REVISTA DE METALURGIA, 1998, 34 (04) : 358 - 373
  • [45] SUBSTITUTION BEHAVIOR OF MN, CR, AND ZR IN TERNARY AND QUATERNARY ALLOYS OF TIAL
    REVIERE, RD
    CHEN, XF
    OLIVER, BF
    BROOKS, CR
    DUNLAP, JR
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1993, 172 (1-2): : 95 - 100
  • [46] Substitution behavior of Mn, Cr, and Zr in ternary and quaternary alloys of TiAl
    Reviere, R.D.
    Chen, X.F.
    Oliver, B.F.
    Brooks, C.R.
    Dunlap, J.R.
    Materials Science and Engineering A, 1993, A172 (1-2) : 95 - 100
  • [47] Precipitation and Recrystallization in Al-(Zr)-(Pr)-(Cr) Alloys
    Fang Huachan
    Chao Hong
    Chen Kanghua
    RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (03) : 599 - 605
  • [48] Primary solidification of ternary compounds in Al-rich Al–Ce–Mn alloys
    Yang, Y.
    Bahl, S.
    Sisco, K.
    Lance, M.
    Shin, D.
    Shyam, A.
    Plotkowski, A.
    Dehoff, R.R.
    Journal of Alloys and Compounds, 2020, 844
  • [49] SOLIDIFICATION PATH OF AL-FE-MN-SI ALUMINIUM ALLOYS
    Eleno, Luiz
    Sundman, Bo
    Lacaze, Jacques
    MODELING OF CASTING, WELDING, AND ADVANCED SOLIDIFICATION PROCESSES - XII, 2009, : 635 - 642
  • [50] Rapid solidification of silver-rich Ag-Cu-Zr alloys
    Castellero, A.
    Kang, D. H.
    Jung, I. -H.
    Angella, G.
    Vedani, M.
    Baricco, M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 536 : S148 - S153
12345