STUDIES ON THE PROPERTIES OF ZIRCONIA FILMS PREPARED BY DIRECT-CURRENT REACTIVE MAGNETRON SPUTTERING

被引：23
|
作者：
SUHAIL, MH
RAO, GM
MOHAN, S
机构：
[1] Instrumentation and services Unit, Indian Institute of Science
来源：
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS | 1991年 / 9卷 / 05期
关键词：
D O I：
10.1116/1.577223
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This paper deals with the preparation of zirconia films by direct current reactive magnetron sputtering. The films were annealed in ambient atmosphere at temperatures ranging from 300 to 850-degrees-C. The as deposited films were found to be amorphous and a crystalline structure developed at 400-degrees-C. The refractive index and extinction coefficient were found to be 1.93 and 0.5 x 10(-3) at 600 nm for the as deposited films and they changed to 1.71 and 2.5 x 10(-3) on annealing at 850-degrees-C. The optical constants were found to be constant in the wavelength region beyond 400 nm, below which dispersion was observed.
引用
收藏
页码：2675 / 2677
页数：3
相关论文
共 50 条
  • [21] THE EFFECT OF TARGET SUBSTRATE COUPLING ON REACTIVE DIRECT-CURRENT MAGNETRON SPUTTERING
    SCHILLER, S
    HEISIG, U
    KORNDORFER, C
    STRUMPFEL, J
    FRACH, P
    SURFACE & COATINGS TECHNOLOGY, 1989, 39 (1-3): : 549 - 564
  • [22] Effects of the sputtering power on the crystalline structure and optical properties of the silver oxide films deposited using direct-current reactive magnetron sputtering
    郜小勇
    张增院
    马姣民
    卢景霄
    谷锦华
    杨仕娥
    Chinese Physics B, 2011, (02) : 374 - 379
  • [23] REACTIVE DIRECT-CURRENT MAGNETRON SPUTTERING OF ALUMINUM-OXIDE COATINGS
    SPROUL, WD
    GRAHAM, ME
    WONG, MS
    LOPEZ, S
    LI, D
    SCHOLL, RA
    JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1995, 13 (03): : 1188 - 1191
  • [24] Solar cells based on copper oxide and titanium dioxide prepared by reactive direct-current magnetron sputtering
    Wisz, G.
    Sawicka-Chudy, P.
    Sibinski, M.
    Starowicz, Z.
    Ploch, D.
    Goral, A.
    Bester, M.
    Cholewa, M.
    Wozny, J.
    Sosna-Glebska, A.
    OPTO-ELECTRONICS REVIEW, 2021, 29 (03) : 97 - 104
  • [25] Effects of the sputtering power on the crystalline structure and optical properties of the silver oxide films deposited using direct-current reactive magnetron sputtering
    Gao Xiao-Yong
    Zhang Zeng-Yuan
    Ma Jiao-Min
    Lu Jing-Xiao
    Gu Jin-Hua
    Yang Shi-E
    CHINESE PHYSICS B, 2011, 20 (02)
  • [26] Optical properties of aluminum-doped zinc oxide films deposited by direct-current pulse magnetron reactive sputtering
    Gao Xiao-Yong
    Chen Chao
    Zhang Sa
    CHINESE PHYSICS B, 2014, 23 (03)
  • [27] Optical properties of aluminum-doped zinc oxide films deposited by direct-current pulse magnetron reactive sputtering
    郜小勇
    陈超
    张飒
    ChinesePhysicsB, 2014, 23 (03) : 205 - 209
  • [28] Evolution of the structural and optical properties of silver oxide films with different stoichiometries deposited by direct-current magnetron reactive sputtering
    Zhao Meng-Ke
    Liang Yan
    Gao Xiao-Yong
    Chen Chao
    Chen Xian-Mei
    Zhao Xian-Wei
    CHINESE PHYSICS B, 2012, 21 (06)
  • [29] Evolution of the structural and optical properties of silver oxide films with different stoichiometries deposited by direct-current magnetron reactive sputtering
    赵孟珂
    梁艳
    郜小勇
    陈超
    陈先梅
    赵显伟
    Chinese Physics B, 2012, 21 (06) : 364 - 367
  • [30] Effect of Argon to Oxygen Ratio on the Properties of Tungsten Oxide Films Prepared by Direct Current Reactive Magnetron Sputtering
    Shi, Ze
    Li, Yue-Chan
    Xie, An
    Sun, Dong-Ya
    JOURNAL OF NANOELECTRONICS AND OPTOELECTRONICS, 2023, 18 (03) : 261 - 273
12345