INTERFACIAL EMBRITTLEMENT IN LIQUID-PHASE SINTERED TUNGSTEN HEAVY ALLOYS

被引：116

作者：

EDMONDS, DV ^{[1
]}

JONES, PN ^{[1
]}

机构：

[1] MINIST DEF,ROYAL ARMAMENT RES & DEV ESTAB,SEVENOAKS TN14 7BP,ENGLAND

来源：

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1979年 / 10卷 / 03期

关键词：

D O I：

10.1007/BF02658336

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The variations in toughness of the liquid-phase sintered heavy alloys W-Ni-Fe and W-Ni-Cu have been examined. Toughness was found to be controlled primarily by the strength of the tungsten particle-matrix interfaces, which is sensitive to the rate of cooling from the sintering temperature. Furnace-cooling led to the embrittlement of these interfaces; in the case of W-Ni-Fe transmission electron microscopy identified interfacial precipitation of a W(NiFe) intermetallic compound, and in W-Ni-Cu Auger electron spectroscopy indicated interfacial segregation of the trace elements phosphorus and sulfur. This embrittlement was effectively reduced by solution treating beneath the sintering temperature and quenching © 1979 American Society for Metals and the Metallurgical Society of AIME.

引用

页码：289 / 295

页数：7

共 12 条

[1]

Ariel E., 1973, POWDER METALL INT, V5, P126

[2]

BRANDON DG, 1971, 5TH P INT S EL MICR, P849

[3]

Ellinger FH., 1940, T AM SOC MET, V28, P619

[4]

GREEN EC, 1956, 58 IR STEEL I SPEC R, P253

[5] PRODUCTION OF TUNGSTEN ALLOY PENETRATION RADIATION SHIELDS [J].

JONES, DJ ;

MUNNERY, P .

POWDER METALLURGY, 1967, 10 (20) :156-&

[6]

JOSHI A, 1970, METALL TRANS, V1, P2543

[7]

KROCK RH, 1964, P PLANSEE SEMINAR, P257

[8]

Price GHS, 1938, J I MET, V62, P239

[9]

TAKEUCHI H, 1967, J JPN I MET, V31, P1064

[10] NEW INTERMETALLIC PHASE IN NICKEL-TUNGSTEN SYSTEM [J].

WALSH, JM ;

DONACHIE, MJ .

METALLURGICAL TRANSACTIONS, 1973, 4 (12) :2854-2855

← 1 2 →