A REVIEW OF FATIGUE CRACK-GROWTH IN STEELS UNDER MIXED MODE-I AND MODE-II LOADING

被引：77

作者：

BOLD, PE ^{[1
]}

BROWN, MW ^{[1
]}

ALLEN, RJ ^{[1
]}

机构：

[1] BRITISH RAIL RES, DERBY DE2 8UP, ENGLAND

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 1992年 / 15卷 / 10期

关键词：

D O I：

10.1111/j.1460-2695.1992.tb00025.x

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The majority of methods for predicting the direction of propagation of mixed mode cracks have assumed that they branch to grow as mode I cracks. However, under some circumstances mode II crack growth occurs. Rolling contact fatigue cracks are one example of an industrial problem where cracks appear to grow under predominantly mode II loading without branching. This paper reviews the available models and the experimental studies in the literature on mixed mode I and II loading, and discusses the parameters that affect the mode of crack growth.

引用

页码：965 / 977

页数：13

共 29 条

[1] SHEAR MODE CRACK-GROWTH AND ROLLING-CONTACT FATIGUE [J].

BOLD, PE ;

BROWN, MW ;

ALLEN, RJ .

WEAR, 1991, 144 (1-2) :307-317

[2]

BOLD PE, 1990, THESIS U SHEFFIELD

[3]

BOLD PE, 1992, IN PRESS FATIGUE C 1

[4]

BOLD PE, 1992, IN PRESS FATIGUE C 2

[5] THE INFLUENCE OF CRACK FACE FRICTION AND TRAPPED FLUID ON SURFACE INITIATED ROLLING-CONTACT FATIGUE CRACKS [J].

BOWER, AF .

JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 1988, 110 (04) :704-711

[6]

Erdogan F., 1963, J BASIC ENG ASME, V85, P519, DOI DOI 10.1115/1.3656897

[7]

HOURLIER F, 1985, ASTM STP, V853, P228

[8] MIXED-MODE FATIGUE THRESHOLDS [J].

HUA, G ;

BROWN, MW ;

MILLER, KJ .

FATIGUE OF ENGINEERING MATERIALS AND STRUCTURES, 1982, 5 (01) :1-17

[9]

HUA G, 1985, ASTM STP, V853, P184

[10]

HUA K, 1979, ACTA METALL SIN, V15, P380

← 1 2 3 →