Self-Irradiation Damage in alpha Plutoninm

被引:5
作者
Hall, R. O. A. [1 ]
Mortimer, M. J. [1 ]
机构
[1] Atom Energy Res Estab, UKAEA Res Grp, Proc Technol Div, Harwell, Berks, England
关键词
D O I
10.1007/BF00628742
中图分类号
O59 [应用物理学];
学科分类号
摘要
The change in the resistivity of high-purity alpha plutonium, due to self-irradiation damage with time of holding in liquid helium, has been measured. A small term, additional to the two terms previously reported, was found. A detailed analysis showed that a good fit was obtained using (rho - rho(0)) = 1.920[1 - exp (-0.65 x 10(-3) t)] - 0.400 [1 - exp (-0.192 x 10(-2) t)] -0.230[1 - exp (-0.172 x 10(-3) t)]mu Omega m This analysis was also applied to earlier results on lower purity alpha plutonium, and to a Pu-1% Np alloy.
引用
收藏
页码:421 / 431
页数:11
相关论文
共 5 条
[1]   COMPARISON OF SELF-IRRADIATION EFFECTS IN ALPHA PLUTONIUM ENRICHED + UNENRICHED IN 238PU [J].
ELLIOTT, RO ;
OLSEN, CE .
JOURNAL OF APPLIED PHYSICS, 1964, 35 (06) :1925-&
[2]  
Griffin C. S., 1968, THESIS
[3]  
King I. E., 1965, P ROY SOC LOND A MAT, V284A, P325
[4]   ETUDE DE LA VARIATION DE LONGUEUR DU PLUTONIUM ALPHA PAR AUTOIRRADIATION A 4 DEGREES K [J].
LALLEMENT, R ;
WIGLEY, DA .
PHYSICA STATUS SOLIDI, 1967, 21 (01) :145-+
[5]   EFFECTS OF IMPURITIES AND SELF-IRRADIATION ON ELECTRICAL RESISTIVITY OF ALPHA-PHASE PLUTONIUM BELOW 300 DEGREES K [J].
OLSEN, CE ;
ELLIOTT, RO .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1962, 23 (SEP) :1225-&