EVALUATING POROSITY PARAMETERS FOR POROSITY PROPERTY RELATIONS

被引:110
作者
RICE, RW
机构
[1] W. R. Grace & Co.‐Conn., Columbia, Maryland
关键词
D O I
10.1111/j.1151-2916.1993.tb06650.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Porosity parameters are considered from the standpoint of a map of the volume fraction porosity (P) and the ratio of normalized radii of the pore (r(p)) and the solid particles, webs, or ligaments (r(s)) defining the pores. For pore structures derived from uniform stacking of identical spherical particles or bubbles, this ''map'' turns out to be a single S-shaped curve showing (1) very significant constraints on porosity variations achievable, and (2) r(p)/r(s) contains no information not already given by P, but (3) P or r(p)/r(s) do not fully characterize the porosity. Of other interrelated porosity factors, i.e, open vs closed or inter- vs intragranular nature, coordination number of the pores or particles, the shape (e.g., curvature) of the pores, and the minimal solid area (i.e., minimum web cross sections or the bond area between particles) representing some porosity characteristics independent of P or r(p)/r(s), it is concluded that the minimum solid area is the most appropriate one. For more complex ideal and real pore structures, (1) the above map starts from the ideal P vs r(p)/r(s) curve at the two extremes of P (0 and 1), but becomes a moderate band in-between, with the ideal P vs r(p)/r(s) curve at or near, the mean of this band, and (2) a second parameter is still needed, and the minimum solid area is still the most appropriate one
引用
收藏
页码:1801 / 1808
页数:8
相关论文
共 36 条
[1]   GRAIN-GROWTH TRANSITION DURING SINTERING OF COLLOIDALLY PREPARED ALUMINA POWDER COMPACTS [J].
CAMERON, CP ;
RAJ, R .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1988, 71 (12) :1031-1035
[2]  
Cumberland D J, 1987, PACKING PARTICLES, V6
[3]  
CYTERMANN R, 1986, FRAGMENTATION FORM F, P458
[5]   MICROSTRUCTURAL EFFECTS ON THE THERMAL-CONDUCTIVITY OF POLYCRYSTALLINE ALUMINUM NITRIDE [J].
ENLOE, JH ;
RICE, RW ;
LAU, JW ;
KUMAR, R ;
LEE, SY .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (09) :2214-2219
[6]  
Gibson L, 1988, CELLULAR SOLIDS STRU
[7]  
GURLAND J, 1958, T AM I MIN MET ENG, V212, P452
[8]  
Heesch H, 1933, Z KRISTALLOGR, V85, P443
[9]  
Horsfield H.T., 1934, J SOC CHEM IND, V53, P107
[10]   MODEL FOR STRENGTH OF BRITTLE POROUS MATERIALS [J].
HRMA, P ;
SATAVA, V .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1974, 57 (02) :71-73