Tensile Properties of Plain Weave Glass Fabric Reinforced Epoxy Resin Laminates at Low Temperatures

被引：1
|
作者：
Kim, Yonjig
机构：
来源：
TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A | 2008年 / 32卷 / 09期
关键词：
Polymer Matrix Composite; Glass Fiber Reinforced Plastic; Autoclave Molding; Plain Weave Prepreg; Tensile Chord Modulus of Elasticity;
D O I：
10.3795/KSME-A.2008.32.9.788
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
To understand the tensile behaviors of GFRP at low temperature, three types of specimen have been used in this study. Tensile properties and fracture mechanisms for three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate were investigated at temperature range of about -30 to 15 degrees C. The tensile properties of axial and edge type specimen decrease slightly with decreasing temperature to -20 degrees C. However, at -30 degrees C the decreases in the tensile properties increased considerably. Below -20 degrees C, thickness type specimen showed a marked decreases in the tensile properties. It was obvious that the fracture manner of thickness type specimen was adhesive failure at above -10 degrees C and a mixed adhesive and cohesive failure at below -20 degrees C.
引用
收藏
页码：788 / 795
页数：8
相关论文
共 19 条
  • [11] Mechanical properties of surface-treated ramie fiber fabric/epoxy resin composite fabricated by vacuum-assisted resin infusion molding with hot compaction
    Xu, Chuanqi
    Gu, Yizhuo
    Yang, Zhongjia
    Li, Min
    Li, Yanxia
    Zhang, Zuoguang
    JOURNAL OF COMPOSITE MATERIALS, 2016, 50 (09) : 1189 - 1198
  • [12] Stress intensity factors for glass-fiber reinforced plastics with an infinite row of parallel cracks at low temperatures
    Sanada, K
    Shindo, Y
    Ueda, S
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 1998, 28 (03) : 183 - 196
  • [13] A comparative study of wear and friction characteristics of glass fibre reinforced epoxy resin, sliding under dry, oil-lubricated and inert gas environments
    Agrawal, Sandeep
    Singh, K. K.
    Sarkar, P. K.
    TRIBOLOGY INTERNATIONAL, 2016, 96 : 217 - 224
  • [14] Mechanical Strength Behaviour of Silane Treated E-glass Fibre/Al 6061 & SS-304 Wire Mesh Reinforced Epoxy Resin Hybrid Composite
    Prakash, V. R. Arun
    Jaisingh, S. Julyes
    SILICON, 2018, 10 (05) : 2279 - 2286
  • [15] Mechanical Strength Behaviour of Silane Treated E-glass Fibre/Al 6061 & SS-304 Wire Mesh Reinforced Epoxy Resin Hybrid Composite
    V. R. Arun Prakash
    S. Julyes Jaisingh
    Silicon, 2018, 10 : 2279 - 2286
  • [16] Role of sugarcane bagasse biogenic silica on cellulosic Opuntia dillenii fibre-reinforced epoxy resin biocomposite: mechanical, thermal and laminar shear strength properties
    Prasad, M. Mohan
    Sutharsan, S. M.
    Ganesan, K.
    Babu, N. Ramesh
    Maridurai, T.
    BIOMASS CONVERSION AND BIOREFINERY, 2023, 13 (18) : 17027 - 17037
  • [17] Role of sugarcane bagasse biogenic silica on cellulosic Opuntia dillenii fibre-reinforced epoxy resin biocomposite: mechanical, thermal and laminar shear strength properties
    M. Mohan Prasad
    S. M. Sutharsan
    K. Ganesan
    N. Ramesh Babu
    T. Maridurai
    Biomass Conversion and Biorefinery, 2023, 13 : 17027 - 17037
  • [18] Low Velocity Impact and Mechanical Behaviour of Shot Blasted SiC Wire-Mesh and Silane-Treated Aloevera/Hemp/Flax-Reinforced SiC Whisker Modified Epoxy Resin Composites
    Murugan, M. Arul
    Jayaseelan, V.
    Jayabalakrishnan, D.
    Maridurai, T.
    Kumar, S. Selva
    Ramesh, G.
    Prakash, V. R. Arun
    SILICON, 2020, 12 (08) : 1847 - 1856
  • [19] Low Velocity Impact and Mechanical Behaviour of Shot Blasted SiC Wire-Mesh and Silane-Treated Aloevera/Hemp/Flax-Reinforced SiC Whisker Modified Epoxy Resin Composites
    M. Arul Murugan
    V. Jayaseelan
    D. Jayabalakrishnan
    T. Maridurai
    S. Selva Kumar
    G. Ramesh
    V. R. Arun Prakash
    Silicon, 2020, 12 : 1847 - 1856
12