摘要：

The role of hydrogen in stress-corrosion cracking (SCC) of austenitic stainless steel was investigated in boiling chloride solution. The tests in the mixed melted salt verified that hydrogen-induced cracking (HIC) could occur at 160 degrees C if sufficient hydrogen could be supplied continuously. It was found that the threshold SCC intensity factors of both 321 and 310 steels were lower than those of HIC during dynamic charging at high fugacity at 40 degrees C and 160 degrees C. In addition, anodic polarization decreased hydrogen concentration and promoted SCC in hot LiCl solution, while cathodic polarization increased hydrogen concentration and restrained SCC. Hydrogen could be introduced into the specimen and be concentrated at the crack tip during SCC. It could promote anodic dissolution and SCC remarkably, although it was not enough to produce cracking.

引用

页码：1777 / 1784

页数：8

共 28 条

[1] THE IN-SITU OBSERVATIONS OF MICROCRACK NUCLEATION AND BLUNTNESS IN DUCTILE FRACTURE [J].

CHEN, QZ ;

CHU, WY ;

HSIAO, CM .

SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (10) :1355-1358

[2]

CHU WY, 1984, CORROSION, V40, P302, DOI 10.5006/1.3581957

[3] STRESS-CORROSION CRACKING IN HIGH-STRENGTH STEEL UNDER MODE-III LOADING [J].

CHU, WY ;

HSIAO, CM ;

XU, BJ .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (04) :711-716

[4] HYDROGEN INDUCED SLOW CRACK-GROWTH IN STABLE AUSTENITIC STAINLESS-STEELS [J].

CHU, WY ;

YAO, J ;

HSIAO, CM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (04) :729-733

[5]

CHU WY, 1984, CORROSION, V49, P487

[6] ION AND LASER MICROPROBES APPLIED TO MEASUREMENT OF CORROSION PRODUCED HYDROGEN ON A MICROSCOPIC SCALE [J].

GRAY, HR .

CORROSION, 1972, 28 (02) :47-&

[7]

KEYS LH, 1974, EFFECT CHEM ENV FRAC, P122

[8]

LAGNEBORG R, 1969, J IRON STEEL I, V207, P363

[9]

Latanision R. M., 1969, FUNDAMENTAL ASPECTS, P214

[10] THE EFFECT OF CRACK-TIP STRAIN RATE AND POTENTIAL ON THE PROPAGATION RATE OF STRESS-CORROSION CRACK FOR 321 STAINLESS-STEEL IN BOILING 42 PCT MGCL2 SOLUTION [J].

LI, D ;

MAO, X .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (10) :2873-2878

← 1 2 3 →