THE CORROSION BEHAVIOR OF NI-AL ALLOYS AND NI-NB-AL ALLOYS IN A H2/H2O/H2S GAS-MIXTURE

被引：3
|
作者：
HE, YR [1 ]
DOUGLASS, DL [1 ]
机构：
[1] UNIV CALIF LOS ANGELES,DEPT MAT SCI & ENGN,LOS ANGELES,CA 90024
来源：
OXIDATION OF METALS | 1993年 / 40卷 / 3-4期
关键词：
MIXED GAS; NI-NB-AL ALLOYS; NI-AL ALLOYS; AL2O3; AL2S3; NINB3S6; NB3S4;
D O I：
10.1007/BF00664497
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The corrosion behavior of two Ni-Al alloys and four Ni-Nb-Al alloys was studied over the temperature range of 600-degrees-C to 1000-degrees-C in a mixed-gas of H-2/H2O/H2S. The parabolic law was generally followed, although linear kinetics were also observed. Multiple-stage kinetics were observed for the Ni-Al alloys. Generally, the scales formed on Ni-13.5Al and Ni-Nb-Al alloys were multilayered, with an outer layer of nickel sulfide with or without pure Ni particles and a complex inner scale. The outer scale became porous and discontinuous with increasing temperature. Very thin scales formed on Ni-31Al. The reduction in corrosion rate with increasing Al content is ascribed to the formation of Al2O3 and Al2S3 in the scale. Platinum markers were found at the interface between the outer and inner scales.
引用
收藏
页码：337 / 371
页数：35
相关论文
共 50 条
  • [41] The corrosion of titanium aluminides in H2/H2S/H2O atmospheres at 800-1000°C
    Kai, W
    Chang, MT
    Bai, CY
    OXIDATION OF METALS, 2001, 56 (3-4): : 191 - 214
  • [42] Corrosion Behaviors of Ni-Cr Alloys in O2, H2O and H2O + O2 Gases at 700°C and the Effect of Temperature
    Chen, Jiarui
    Jiang, Chengyang
    Zhang, Jianqiang
    HIGH TEMPERATURE CORROSION OF MATERIALS, 2023, 100 (5-6) : 775 - 789
  • [43] Corrosion of Fe-(4.8,9.2,14.3) Wt%Al alloys at 700 and 800 A°C in N2/H2O/H2S gases
    Kim, Min Jung
    Lee, Dong Bok
    METALS AND MATERIALS INTERNATIONAL, 2013, 19 (05) : 975 - 982
  • [44] High temperature corrosion behavior of iron aluminides containing ternary additions in H2/H2S/H2O mixed gases
    Kai, W
    Chu, JP
    Huang, RT
    Lee, PY
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 240 : 859 - 870
  • [45] High temperature corrosion mechanisms of certain new TiAl-based intermetallic alloys in an aggressive H2/H2O/H2S environment at 850°C
    Du, H. L.
    Datta, P. K.
    Hu, D.
    Wu, X.
    CORROSION SCIENCE, 2007, 49 (05) : 2406 - 2420
  • [46] H2 Generation from H2O and H2S through an Iodine Cycle
    Gillis, Ryan J.
    Lolur, Phalgun
    Green, William H.
    ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2019, 7 (07) : 7369 - 7377
  • [47] THE CORROSION BEHAVIOR OF CO-MO ALLOYS IN H2-H2O-H2S ENVIRONMENTS
    SHING, CC
    DOUGLASS, DL
    GESMUNDO, F
    OXIDATION OF METALS, 1992, 37 (5-6): : 441 - 461
  • [48] Degradation Effects of Ni Patterned Anodes in H2/H2O Atmosphere
    Utz, A.
    Stoermer, H.
    Leonide, A.
    Weber, A.
    Ivers-Tiffee, E.
    SOLID OXIDE FUEL CELLS 11 (SOFC-XI), 2009, 25 (02): : 2013 - 2021
  • [49] SULFIDATION BEHAVIOR OF FE-25CR-20NI-3SI IN H2/H2O/H2S/AR AT 700-DEGREES-C
    SRINIVASAN, V
    PADGETT, RA
    CHOUDHURY, A
    CORROSION, 1991, 47 (09) : 703 - 712
  • [50] CORROSION BEHAVIOR OF CR2O3 - FORMER ALLOYS IN H2-H2S-H2O ATMOSPHERES
    HINDAM, H
    WHITTLE, DP
    CORROSION, 1982, 38 (01) : 33 - 39
12345