CORROSION FATIGUE PROCESS OF 12 CR STAINLESS-STEEL

被引：17
|
作者：
EBARA, R [1 ]
YAMADA, T [1 ]
KAWANO, H [1 ]
机构：
[1] MITSUBISHI HEAVY IND CO LTD,NAGASAKI RES & DEV CTR,NAGASAKI 85019,JAPAN
来源：
ISIJ INTERNATIONAL | 1990年 / 30卷 / 07期
关键词：
12Cr stainless steel; corrosion fatigue; image analyzing technology; microfractography; corrosion pit; turbine blade;
D O I：
10.2355/isijinternational.30.535
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Microfractographical features of corrosion fatigue process of 12 Cr stainless steel turbine blade material are described. The emphasis is focussed upon the initiation and growth of corrosion pits in corrosion fatigue crack initiation process. A quantitative analyzed example of corrosion pit by use of recent developed image analyzing technology is also touched in brief. © 1990, The Iron and Steel Institute of Japan. All rights reserved.
引用
收藏
页码：535 / 539
页数：5
相关论文
共 50 条
  • [21] Evaluation of stress corrosion cracking and corrosion fatigue crack growth characteristics for martensitic stainless steel
    Inoue T.
    Sakaue K.
    Hideo C.H.O.
    Ogawa T.
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2010, 76 (772): : 1698 - 1704
  • [22] Modelling of corrosion fatigue crack initiation on martensitic stainless steel in high cycle fatigue regime
    El May, Mohamed
    Saintier, Nicolas
    Palin-Luc, Thierry
    Devos, Olivier
    Brucelle, Olivier
    CORROSION SCIENCE, 2018, 133 : 397 - 405
  • [23] Stress corrosion cracking and corrosion fatigue cracking of a duplex stainless steel in white water environments
    Singh, PM
    Perdomo, JJ
    Oteng, JE
    Mahmood, J
    CORROSION, 2004, 60 (09) : 852 - 861
  • [24] THE CORROSION FATIGUE CRACK PROPAGATION OF 316LN AUSTENITIC STAINLESS STEEL
    Yang, Bin
    Wu, Huanchun
    7TH INTERNATIONAL CONFERENCE INTEGRITY-RELIABILITY-FAILURE (IRF2020), 2020, : 321 - 322
  • [25] Corrosion Fatigue Behavior of Duplex Stainless Steel in 3.5% Sodium Chloride Solution
    S. H Abubakir
    Journal of University of Science and Technology Beijing(English Edition), 2001, (02) : 133 - 136
  • [26] Corrosion fatigue behavior of duplex stainless steel in 3.5% sodium chloride solution
    Abubakir, SH
    Wu, YS
    Ding, BF
    Li, JQ
    Cao, B
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2001, 8 (02): : 133 - 136
  • [27] IMPROVING CORROSION FATIGUE & DAMAGE PERFORMANCE OF 410 STAINLESS STEEL VIA LPB
    Hornbach, Douglas J.
    Scheel, Jeremy E.
    INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION - 2012, VOL 3, PTS A-C: DESIGN, MATERIALS, AND MANUFACTURING, 2013, : 737 - 744
  • [28] Corrosion fatigue crack initiation behavior of stainless steels
    Ebara, Ryuichiro
    FATIGUE 2010, 2010, 2 (01): : 1297 - 1306
  • [29] Influence of environment on the fatigue crack growth behaviour of 12% Cr steel
    Schoenbauer, Bernd M.
    Stanzl-Tschegg, Stefanie E.
    ULTRASONICS, 2013, 53 (08) : 1399 - 1405
  • [30] Evaluation of corrosion fatigue crack initiation life of 13Cr steel
    Kim, WonBeom
    Paik, JeomKee
    Yajima, Hiroshi
    Experimental Mechanics in Nano and Biotechnology, Pts 1 and 2, 2006, 326-328 : 1007 - 1010
12345