DISLOCATION CHARACTERIZATION IN CRYSTALS OF POTASH ALUM GROWN BY SEEDED SOLUTION GROWTH UNDER CONDITIONS OF LOW SUPERSATURATION

An analysis has been carried out of the genesis and character of growth dislocations present in all growth sectors of single crystals of potash alum. The crystals, grown from seeded solutions by the temperature lowering method under conditions of low supersaturation, presented the well-developed forms: {111} dominant, {100} and {110}. Growth dislocations formed predominately during refacetting of the edges and corners of the seed, rounded during preparation and insertion into the supersaturated solution, From here they become refracted into the (111) sectors which proved to be the most defective. Smaller numbers of dislocations form at the {111}, {100} and {110} seed interfaces and propagate in these sectors. In crystals of inferior quality, a number of inclusions were found predominantly in the fast growing {100) sectors which become the source of additional dislocations. Dislocations present in the original seed did not propagate across the interface into the developing crystal. Dislocations of all characters were observed. The principal Burgers vectors were found to be [100], [110] and [111].