PROCESSING PARAMETERS FOR FILAMENT WINDING THICK-SECTION PEEK CARBON-FIBER COMPOSITES

The consolidation pressure and winding speed for thermoplastic filament winding were studied. Thermoplastic composite parts were manufactured from tape prepreg (APC-2); powder-coated, semi-consolidated towpreg; and commingled fiber towpreg. The material used was carbon fiber (AS-4) (60 vol%) in a PEEK matrix. The parts made were open-ended cylinders of the three materials, 177.8-mm ID, 228.6 mm long, 17 plies thick with a 0-degrees lay-up angle; and rings, 50 plies of APC-2 thick, 6.35 mm wide (one strip wide), 177.8-mm ID, and a lay-up of 0-degrees. Their quality was determined by surface finish and void percentage. The tubes made from APC-2 appeared to have the best quality of the three prepregs. For the rings, the speed of lay-down had a significant effect (at a 99% confidence level) on both the final width of the parts and on the percentage of voids. The pressure of the roller had a significant effect on the final widths at a 99% confidence level, but a significant effect on the percentage of voids at only a 95% confidence level.