MOSSBAUER STUDY OF THE KINETIC-BEHAVIOR OF ANOMALOUS AUSTENITE FORMATION IN FE-12CR-4NI STEEL

被引：4
|
作者：
VARGA, I
KUZMANN, E
KALDOR, M
VERTES, A
机构：
[1] Department of Nuclear Chemistry, Eötvös University, Budapest 112, H-1518
来源：
JOURNAL OF RADIOANALYTICAL AND NUCLEAR CHEMISTRY-LETTERS | 1992年 / 165卷 / 02期
关键词：
D O I：
10.1007/BF02164262
中图分类号：
O65 [分析化学];
学科分类号：
070302 ; 081704 ;
摘要：
Mossbauer spectroscopy was used in order to get information about the anomalous austenite formation1 taking place between 450-600 degrees-C in steel containing 12%Cr and 4%Ni. Even below the equilibrium transition temperature (640-degrees-C) of alpha-->gamma transformation a monotonic increase of the relative spectral area of the line belonging to austenite was observed in the Mossbauer spectra of the steel isothermally aged at 550-degrees-C with increasing ageing time. At the same time, the Cr content of the ferrite phase decreases. Time dependence of the quantity of austenite formed during the isothermal ageing follows the Avrami-kinetics with an exponent n=0.3.
引用
收藏
页码：115 / 126
页数：12
相关论文
共 50 条
  • [21] The formation of isothermal martensite in a 12Cr-9Ni-4Mo maraging stainless steel
    Nilsson, JO
    Larsson, T
    Holmquist, M
    CORROSION REVIEWS, 1999, 17 (02): : 131 - 136
  • [22] The formation of isothermal martensite in a 12Cr-9Ni-4Mo maraging stainless steel
    Nilsson, JO
    Holmquist, M
    Larsson, T
    EUROMAT 97 - PROCEEDINGS OF THE 5TH EUROPEAN CONFERENCE ON ADVANCED MATERIALS AND PROCESSES AND APPLICATIONS: MATERIALS, FUNCTIONALITY & DESIGN, VOL 1: METALS AND COMPOSITES, 1997, : 491 - 494
  • [23] Investigation of the evolution of retained austenite in Fe-13%Cr-4%Ni martensitic stainless steel during intercritical tempering
    Zhang, Shenghua
    Wang, Pei
    Li, Dianzhong
    Li, Yiyi
    MATERIALS & DESIGN, 2015, 84 : 385 - 394
  • [24] Enhanced toughness of Fe–12Cr–5.5Ni–Mo-deposited metals through formation of fine reversed austenite
    Shipin Wu
    Dongpo Wang
    Chen Zhao
    Zhi Zhang
    Chengning Li
    Xinjie Di
    Journal of Materials Science, 2018, 53 : 15679 - 15693
  • [25] Study on the crystallographic orientation relationship and formation mechanism of reversed austenite in economical Cr12 super martensitic stainless steel
    Ye, Dong
    Li, Shaohong
    Li, Jun
    Jiang, Wen
    Su, Jie
    Zhao, Kunyu
    MATERIALS CHARACTERIZATION, 2015, 109 : 100 - 106
  • [26] ISOTHERMAL FORMATION OF MARTENSITE IN A 12CR-9NI-4MO MARAGING STAINLESS-STEEL
    HOLMQUIST, M
    NILSSON, JO
    STIGENBERG, AH
    SCRIPTA METALLURGICA ET MATERIALIA, 1995, 33 (09): : 1367 - 1373
  • [27] Experimental kinetic study of interdiffusion behavior and intermetallic compound Zr(Fe,Cr)2 formation at the Cr/Zry4 interface under elevated temperatures
    Li B.
    Yang H.
    Holmes R.
    Cui L.
    Kano S.
    Abe H.
    Journal of Nuclear Materials, 2023, 584
  • [28] Variation of the Reversed Austenite Amount with the Tempering Temperature in a Fe-13%Cr-4%Ni-Mo Martensitic Stainless Steel
    Song, Yuanyuan
    Li, Xiuyan
    Yin, Fuxing
    Ping, Dehai
    Rong, Lijian
    Li, Yiyi
    ENERGY AND ENVIRONMENT MATERIAL S, 2010, 650 : 193 - +
  • [29] Effects of Various Post-Weld Heat Treatments on Austenite and Carbide Formation in a 13Cr4Ni Steel Multipass Weld
    Amrei, Mohsen Mokhtabad
    Monajati, Hossein
    Thibault, Denis
    Verreman, Yves
    Bocher, Philippe
    METALLOGRAPHY MICROSTRUCTURE AND ANALYSIS, 2016, 5 (01) : 50 - 61
  • [30] In situ investigation on the deformation-induced phase transformation of metastable austenite in Fe-13% Cr-4% Ni martensitic stainless steel
    Zhang, Shenghua
    Wang, Pei
    Li, Dianzhong
    Li, Yiyi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 635 : 129 - 132
12345