WIDE TEMPERATURE SPECTRUM SELF-LUBRICATING COATINGS PREPARED BY PLASMA SPRAYING

Self-lubricating, multicomponent coatings, which lubricate over a wide range of operating conditions, are described. The coatings have been successfully applied by plasma spraying mixed powders onto superalloy substrates. They have been evaluated in friction and wear experiments and in sliding contact bearing tests. These coatings are wear resistant by virtue of their self-lubricating characteristics rather than because of extreme hardness; a further benefit is low friction. Experiments with simple pin-on-disk sliding specimens and oscillating plain cylindrical bearing tests were performed to evaluate the tribological properties of the coatings. It was shown that coatings of Nichrome, glass and calcium fluoride are self-lubricating from about 500 to 900°C, but give high friction at the lower temperatures. The addition of silver to the coating composition improved the low temperature bearing properties and resulted in coatings which are self-lubricating from cryogenic temperatures to at least 870°C; they are therefore wide temperature spectrum" self-lubricating compositions. © 1979."