REMOVAL OF CHROMIUM FROM MOLTEN STEEL BY OXIDATION REFINING

被引：1
|
作者：
MAYA, K
MATSUO, T
机构：
[1] Sumitomo Metal Industries Ltd, Amagasaki
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1991年 / 77卷 / 03期
关键词：
REMOVAL OF CHROMIUM; TRAMP ELEMENT; OXIDATION REFINING; SECONDARY REFINING; SCRAP;
D O I：
10.2355/tetsutohagane1955.77.3_369
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Removal of chromium from molten steel is investigated with (CaO-MgO-MnO2)-(SiO2-Al2O3)-Fe2O3 flux in a laboratory scale test. By using the flux of about 50 kg/t, chromium 60 to 75% is removed from molten steel by oxidation refining, if (1) FeO activity is high, (2) slag basicity, (CaO + MgO + MnO)/(SiO2 + Al2O3) is 1.5 to 2.0, and (3) MgO is added to the flux as a component for accelerating removal of chromium. In addition, manganese loss in this treatment is suppressed, if (1) MnO2 is added to the flux or (2) carbon is added to the slag after removal of chronium.
引用
收藏
页码：369 / 376
页数：8
相关论文
共 50 条
  • [1] OXIDATION DEPHOSPHORIZING METHOD OF MOLTEN STEEL CONTAINING CHROMIUM
    MIZUKAMI, Y
    TSUTSUMI, N
    SHIMA, H
    HORI, T
    KOMAI, T
    TAKAISHI, S
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1988, 74 (02): : 286 - 293
  • [2] DEPHOSPHORIZATION OF MOLTEN STEEL CONTAINING CHROMIUM (PRODUCTION OF CLEAN STEEL BY LADLE REFINING TECHNOLOGY - III).
    Murata, Hironobu
    Mizukami, Yoshimasa
    Tsutsumi, Naoto
    Shima, Hiroshi
    Hori, Toshio
    Takaishi, Shogo
    Transactions of the Iron and Steel Institute of Japan, 1985, 25 (11)
  • [3] Mechanism of inclusion removal from molten steel by bubbles during the refining process with argon blowing
    Zheng, Shu-Guo
    Zhu, Miao-Yong
    Kang T'ieh/Iron and Steel (Peking), 2008, 43 (06): : 25 - 29
  • [4] PRODUCTION OF CLEAN STEEL BY LADLE REFINING TECHNOLOGY .3. A DEPHOSPHORIZATION OF MOLTEN STEEL CONTAINING CHROMIUM
    TSUTSUMI, N
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (04): : S192 - S192
  • [5] PRODUCTION OF CLEAN STEEL BY LADLE REFINING TECHNOLOGY .3. A DEPHOSPHORIZATION OF MOLTEN STEEL CONTAINING CHROMIUM
    MURATA, H
    MIZUKAMI, Y
    TSUTSUMI, N
    SHIMA, H
    HORI, T
    TAKAISHI, S
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (11) : B295 - B295
  • [6] The Arsenic Removal From Molten Steel
    Wang, JianJun
    Luo, Lingen
    Kong, Hui
    Zhou, Li
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2011, 30 (1-2) : 171 - 173
  • [7] Removal of Residual Element Antimony from Molten Steel by CaC2-Containing Refining Slag
    Chen, Zihong
    Liu, Mengke
    Ma, Guojun
    Zhang, Xiang
    Du, Tianyu
    Xue, Zhengliang
    METALS, 2023, 13 (03)
  • [8] Activity of Chromium Oxide in Calcium Silicate Bearing Molten Slag for Highly Clean Chromium Steel Refining Process
    Liu, Yuxing
    Li, Zhi
    Kobayashi, Yoshinao
    ISIJ INTERNATIONAL, 2023, 63 (02) : 313 - 318
  • [9] Oxidation and reduction of chromium in the process of argon-oxygen refining of stainless steel
    Povolotskii, DY
    Zyryanov, SV
    STEEL IN TRANSLATION, 1995, 25 (07) : 35 - 38
  • [10] Copper Removal from Molten Steel by Gasification
    Li Liansheng
    Li Shiqi
    Xiang Changxiang
    Cao Jie
    Liu Keming
    Li Suqin
    Journal of Iron and Steel Research(International), 1999, 6 (02) : 10 - 13
12345