SLIDING BEHAVIOR OF ALUMINUM

被引：79
作者：
KUO, SM [1 ]
RIGNEY, DA [1 ]
机构：
[1] OHIO STATE UNIV,COLUMBUS,OH 43210
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1992年 / 157卷 / 02期
关键词：
D O I：
10.1016/0921-5093(92)90020-2
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The behavior of aluminum pins (high purity aluminum, aluminum alloy 1100 and Al-1at.%Mg) sliding in vacuum against rotating disks of M2 tool steel was investigated for a range of sliding speeds. Wear of these ductile materials occurs mainly by extrusion at the exit side of the wear scar. Friction at steady state is similar for all three materials. For high purity aluminum at low sliding speeds, the spacing of lamellae which appear on the surface is the same as the spacing between microbands revealed by transmission electron microscopy. This and other observations of deformation substructure can be accommodated by Rosenfield's theory of shear instability in sliding wear. Recrystallization is also observed, but it does not seem to have a large effect on the friction and wear behavior for the conditions used in these tests.
引用
收藏
页码：131 / 143
页数：13
相关论文
共 65 条
  • [1] SHEAR-BAND ORIENTATIONS IN PLANE-STRAIN
    ANAND, L
    SPITZIG, WA
    [J]. ACTA METALLURGICA, 1982, 30 (02): : 553 - 561
  • [2] Archard JF., 1959, WEAR, V2, P438, DOI [10.1016/0043-1648(59)90159-0, DOI 10.1016/0043-1648(59)90159-0]
  • [3] A COMPARATIVE INVESTIGATION OF SURFACE RELIEF STRUCTURES AND DISLOCATION MICROSTRUCTURES IN COLD-ROLLED ALUMINUM
    BARLOW, CYJ
    BAY, B
    HANSEN, N
    [J]. PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1985, 51 (02): : 253 - 275
  • [4] DEFORMATION STRUCTURES IN LIGHTLY ROLLED PURE ALUMINUM
    BAY, B
    HANSEN, N
    KUHLMANNWILSDORF, D
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 113 : 385 - 397
  • [5] EFFECT OF INITIAL GRAIN-SIZE ON DYNAMIC RECRYSTALLIZATION OF COPPER
    BLAZ, L
    SAKAI, T
    JONAS, JJ
    [J]. METAL SCIENCE, 1983, 17 (12): : 609 - 616
  • [6] BROWN K, 1972, J I MET, V100, P341
  • [7] A STUDY OF SHEAR DEFORMATION AND WORK-HARDENING OF METALS UNDER PRESSURES TO 2100-MPA
    CAI, BC
    KUHLMANNWILSDORF, D
    NELSON, RB
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 138 (01): : 33 - 47
  • [8] CHEN LH, 1984, THESIS OHIO STATE U
  • [9] EFFECT OF STRAIN RATE ON THE DISLOCATION SUBSTRUCTURE IN DEFORMED COPPER POLYCRYSTALS
    CHEVAL, F
    PRIESTER, L
    [J]. SCRIPTA METALLURGICA, 1989, 23 (11): : 1871 - 1876
  • [10] THE ROLE OF DYNAMIC RECRYSTALLIZATION IN DRY SLIDING WEAR
    DAUTZENBERG, JH
    [J]. WEAR, 1980, 60 (02) : 401 - 411
1234567