PHASE EVOLUTION AND ANNEALING EFFECTS ON THE ELECTRICAL-PROPERTIES OF PB(ZR0.53TI0.47)O-3 THIN-FILMS WITH RUO2 ELECTRODES

被引：64

作者：

ALSHAREEF, HN ^{[1
]}

BELLUR, KR ^{[1
]}

AUCIELLO, O ^{[1
]}

KINGON, AI ^{[1
]}

机构：

[1] MCNC,DIV ELECTR TECHNOL,RES TRIANGLE PK,NC 27709

来源：

THIN SOLID FILMS | 1995年 / 256卷 / 1-2期

关键词：

DIELECTRICS; ELECTRICAL PROPERTIES AND MEASUREMENTS; RUTHENIUM; SURFACE MORPHOLOGY;

D O I：

10.1016/0040-6090(94)06318-4

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The electrical properties and crystallization of Pb(Zr0.53Ti0.47)O-3 (PZT) thin films grown on RuO2 electrodes by the sol-gel process have been studied. It was found that the amorphous as-deposited thin film first transforms to a pyrochlore phase at 500 degrees C. On further annealing, perovskite PZT begins to crystallize at about 600 degrees C. TEM anlysis reveals that a pyrochlore-type second phase still exists in the films even after annealing to temperatures of 750 degrees C for 10 min. These PZT films are fatigue-free, but they show large property variation and high leakage currents (J = 10(-3) A cm(-2) at 1 V). An 800 degrees C annealing treatment, for 10 min in air, of the RuO2 bottom electrode prior to film deposition enhanced perovskite PZT nucleation, thereby eliminating the pyrochlore-type second phase. In addition, the leakage currents of PZT films grown on annealed RuO, electrodes are about two orders of magnitude lower than those of PZT films grown on unannealed RuO2. It is also observed that annealing the entire capacitor stack after the top electrode deposition improved capacitor properties.

引用

页码：73 / 79

页数：7

共 16 条

[1]

Al-Shareef H. N., 1994, Ferroelectrics, V152, P85, DOI 10.1080/00150199408017601

[2]

Al-Shareef H. N., 1993, Integrated Ferroelectrics, V3, P321, DOI 10.1080/10584589308216687

[3]

ALSHAREEF HN, 1994, UNPUB 6TH INT S INT

[4]

ALSHAREEF HN, IN PRESS THIN SOLID

[5]

ALSHAREEF HN, 1993, IN PRESS 5TH INT S I

[6]

ASLSHAREEF HN, 1991, CERAMIC T, V25, P97

[7]

BELLUR KR, 1992, 8TH P IEEE INT S APP, P448

[8]

BERNSTEIN SD, 1992, J MATER RES, V8, P12

[9]

CHEN X, 1993, IN PRESS 5TH INT S I

[10] FABRICATION AND PROPERTIES OF EPITAXIAL FERROELECTRIC HETEROSTRUCTURES WITH (SRRUO3) ISOTROPIC METALLIC OXIDE ELECTRODES [J].

EOM, CB ;

VANDOVER, RB ;

PHILLIPS, JM ;

WERDER, DJ ;

MARSHALL, JH ;

CHEN, CH ;

CAVA, RJ ;

FLEMING, RM ;

FORK, DK .

APPLIED PHYSICS LETTERS, 1993, 63 (18) :2570-2572

← 1 2 →