INDENTATION CRACK-SHAPE EVOLUTION DURING SUBCRITICAL CRACK-GROWTH

被引:19
作者
DWIVEDI, P
GREEN, DJ
机构
[1] Department of Materials Science and Engineering, Pennsylvania State University, University Park, Pennsylvania
关键词
D O I
10.1111/j.1151-2916.1995.tb08476.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Indentation crack-shape evolution during subcritical crack growth was examined in soda-lime glass, Crack-arrest markings were generated on the fracture surfaces by temporary unloading during subcritical crack growth, Crack shapes were determined from these crack-arrest markings by optical microscopy, The shapes were found to be semielliptical, but the ellipticity changed significantly with crack extension under an applied bending stress, Crack-shape evolution was predicted by using the stress intensity factor equation for a semielliptical crack for the applied stress distribution and the subcritical crack growth parameters for the material/environment system. Experimental results were found to be in excellent agreement with the predictions, The influence of the initial crack size and shape, the loading configuration, and the subcritical crack growth exponent n on crack-shape evolution was also investigated in the simulations, It was found that, for the particular loading configuration and material, there is an equilibrium shape associated with the subcritically growing crack. The variation in crack shape with its extension during subcritical crack growth was found to be an important factor in lifetime prediction.
引用
收藏
页码:1240 / 1246
页数:7
相关论文
共 26 条
[1]   EFFECTS OF ELECTRIC-FIELDS ON SLOW CRACK-GROWTH IN GLASS [J].
CASO, GB ;
SCHWABEL, MG ;
FRECHETTE, V .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (01) :43-48
[2]   RELATION BETWEEN MULTIREGION CRACK-GROWTH AND DYNAMIC FATIGUE OF GLASS USING INDENTATION FLAWS [J].
CHANTIKUL, P ;
LAWN, BR ;
RICHTER, H ;
FREIMAN, SW .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1983, 66 (07) :515-518
[3]  
DWIVEDI P, IN PRESS J AM CERAM
[4]  
GONG JH, 1992, FRACT MECH, V9, P569
[5]   CRACK EVOLUTION IN VICKERS INDENTATION FOR SODA-LIME SILICA GLASS [J].
HARANOH, T ;
ISHIKAWA, H ;
SHINKAI, N ;
MIZUHASHI, M .
JOURNAL OF MATERIALS SCIENCE, 1982, 17 (05) :1493-1500
[6]  
JONES SL, 1987, J MATER SCI, V22, P721
[7]  
KAWAI M, 1977, FRACTURE MECHANICS C, V6, P587
[8]  
KERKHOF F, 1969, FRACTURE
[9]   THRESHOLD MICROFRACTURE DURING ELASTIC-PLASTIC INDENTATION OF CERAMICS [J].
LANKFORD, J .
JOURNAL OF MATERIALS SCIENCE, 1981, 16 (05) :1177-1182
[10]  
LAUGIER MT, 1986, I PHYSICS C SERIES, V75, P449