CORROSION CHARACTERISTICS OF TIN-COATED CARBON-STEELS IN ACIDS AND CHLORIDE SOLUTIONS

被引:8
|
作者
YAMAGUCHI, S [1 ]
HARA, N [1 ]
SUGIMOTO, K [1 ]
机构
[1] TOHOKU UNIV, FAC ENGN, DEPT MET, SENDAI, MIYAGI 980, JAPAN
关键词
TIN FILM; REACTIVE SPUTTERING; CORROSION RESISTANCE; CARBON STEEL; ANODIC POLARIZATION CURVE; IMMERSION TEST; CORROSION RATE; GALVANIC COUPLING;
D O I
10.2320/jinstmet1952.56.3_294
中图分类号
学科分类号
摘要
Electrochemical polarization and corrosion properties of carbon steels having TiN films 0.1-10-mu-m thick formed by reactive sputtering have been examined in 1 kmol.m-3 H2SO4, 1 kmol.m-3 HCl and 3 mass%NaCl, comparing with those of TiN prepared on Ti plates by nitriding. It was found that the corrosion resistance of the TiN-coated steels in short-range immersion in the solutions was improved with increasing thickness of TiN film, d(TiN): In 1 kmol.m-3 H2SO4, an active dissolution current density at 0.1 V (vs. Ag/AgCl-3.33 kmol.m-3 KCl) decreased by a factor of 1000 as d(TiN) increased from 0.1 to 8-mu-m, and the corrosion rate measured after immersion for 84.6 ks decreased correspondingly. In 3 mass%NaCl, a sharp increase in current due to pitting was observed on the anodic polarization curves of the steels having d(TiN) < 6-mu-m. No such increase, however, was observed on the curves of the steel having d(TinN > 8-mu-m. The improvement of corrosion resistance with increasing d(TiN) can be attributed to the decrease in the amount of open pin-holes in TiN films. After prolonged immersion, the steels covered with thicker TiN films also suffered from pitting corrosion because of the penetration of the solutions through microdefects in the films. From the measurement of cathodic polarization curves of TiN and galvanic current densities of carbon steels coupled to TiN, it was found that in an aerated NaCl solution the TiN films on carbon steels acted as cathodic sites and thus galvanic corrosion occurred on the steel substrates. In a deaerated H2SO4 solution, however, no galvanic corrosion was presumed to occur because the hydrogen overvoltage of TiN was fairly large in this solution.
引用
收藏
页码:294 / 302
页数:9
相关论文
共 50 条
  • [11] CORROSION AND POTENTIOSTATIC HYDROGENATION OF CARBON-STEELS IN CARBONATE-SULFATE SOLUTIONS
    FROLOVA, LB
    FOKIN, MN
    ZORINA, VE
    PROTECTION OF METALS, 1994, 30 (03): : 212 - 214
  • [12] An experimental investigation of the survivability and friction characteristics of tin-coated and polymer-laminated steels
    Jaworski, J
    Schmid, SR
    Wang, JE
    JOURNAL OF MANUFACTURING SCIENCE AND ENGINEERING-TRANSACTIONS OF THE ASME, 1999, 121 (02): : 232 - 237
  • [13] Metallic biomaterials TiN-coated:: Corrosion analysis and biocompatibility
    Paschoal, AL
    Vanâncio, EC
    Canale, LDF
    da Silva, OL
    Huerta-Vilca, D
    Motheo, AD
    ARTIFICIAL ORGANS, 2003, 27 (05) : 461 - 464
  • [14] OXIDATION AND CORROSION OF TIN-COATED ZIRCALOY-4
    HAUFFE, K
    MARTINEZ, V
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1976, 123 (05) : 595 - 602
  • [15] Simulation for fretting corrosion of tin-coated copper contacts
    Lee, K. Y.
    Jeong, D. K.
    Joo, H. G.
    Park, Y. W.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2011, 62 (04): : 352 - 356
  • [16] Corrosion behavior of TiN-coated 304 stainless steel
    Chou, WJ
    Yu, GP
    Huang, JH
    CORROSION SCIENCE, 2001, 43 (11) : 2023 - 2035
  • [17] Corrosion behavior of TiN-coated cutting carbide tools
    Belhamra, Nadjette
    Chala, Abdelouahed
    MAIN GROUP CHEMISTRY, 2014, 13 (01) : 65 - 71
  • [18] Analysis of Corrosion Characteristics for TiN- and Ti/TiN-coated Stainless Steel Bipolar Plate in PEMFC
    Han, Choonsoo
    Chae, Gil-Byung
    Lee, Chang-Rae
    Choi, Dae-Kyu
    Shim, Joongpyo
    KOREAN CHEMICAL ENGINEERING RESEARCH, 2012, 50 (01): : 118 - 127
  • [19] CRACKING OF CARBON-STEELS IN ALKALI SOLUTIONS
    KARPENKO, GV
    VASILENK.II
    MELEKHOV, RK
    CHAPLYA, ON
    DYADCHEN.BT
    DOKLADY AKADEMII NAUK SSSR, 1972, 202 (03): : 649 - &
  • [20] DISSOLUTION OF CARBON-STEELS IN SOLUTIONS OF HYDROCHLORIC-ACID AND FERRIC-CHLORIDE
    KOCHERGIN, VP
    MOISEEVA, TF
    ZAGURSKAYA, IN
    ROMANOVA, GA
    AZAROVA, VI
    JOURNAL OF APPLIED CHEMISTRY OF THE USSR, 1979, 52 (04): : 893 - 895