Corrosion Failures in Gas Turbine Hot Components

被引：0
|
作者：
Kosieniak, E. [1 ]
Biesiada, K. [2 ]
Kaczorowski, J. [2 ]
Innocenti, M. [3 ]
机构：
[1] Warsaw Inst Aviat, Warsaw, Poland
[2] Gen Elect Co Polska Spzoo, Warsaw, Poland
[3] Gen Elect Nouvo Pignone SPA, Florence, Italy
来源：
JOURNAL OF FAILURE ANALYSIS AND PREVENTION | 2012年 / 12卷 / 03期
关键词：
Failure analysis; Hot corrosion; Superalloys; Gas turbine hot gas path;
D O I：
10.1007/s11668-012-9571-3
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
At elevated temperatures hot corrosion often takes place in gas turbines and other combustion turbo-machinery. The main corrosion issues are high-temperature environmental attack in the form of high-temperature oxidation and hot corrosion. Two case histories of gas turbine hot components are presented. The mechanisms for different types of hot corrosion are discussed. The influence of temperature, composition, and microstructure of materials on hot corrosion is described. A variety of practical approaches to minimize hot corrosion are considered.
引用
收藏
页码：330 / 337
页数：8
相关论文
共 50 条
  • [21] Hot corrosion resistance of gas turbine materials in combusted syngas environments
    Sumner, J.
    Potter, A.
    Simms, N. J.
    Oakey, J. E.
    MATERIALS AT HIGH TEMPERATURES, 2015, 32 (1-2) : 177 - 187
  • [22] Hot corrosion resistance of gas turbine materials in combusted syngas environments
    Cranfield University, Cranfield, Bedfordshire
    MK43 0FD, United Kingdom
    Energy Mater. Mater. Sci. Eng. Energy Syst., 1 (177-187):
  • [23] Hot Corrosion of Plasma Sprayed Coatings for Waste Gas Turbine Blades
    廖小宁
    叶锐曾
    吕反修
    孙金贵
    张乃平
    北京科技大学学报, 1989, (06) : 551 - 559
  • [24] Ceramic composite development for gas turbine engine hot section components
    DiCarlo, James A.
    van Roode, Mark
    Proceedings of the ASME Turbo Expo 2006, Vol 2, 2006, : 221 - 231
  • [25] CONSIDERATIONS FOR DAMAGE ANALYSIS OF GAS-TURBINE HOT SECTION COMPONENTS
    COOK, TS
    LAFLEN, JH
    MECHANICAL ENGINEERING, 1984, 106 (09) : 115 - 116
  • [26] Materials and coatings for industrial gas turbine components exposed to hot gases
    Bétis, F
    JOURNAL DE PHYSIQUE IV, 2000, 10 (P4): : 15 - 22
  • [27] HOT CORROSION IN TURBINE MATERIALS
    HAMILTON, PE
    ALLISON RESEARCH AND ENGINEERING, 1966, 11 (Q3): : 11 - &
  • [28] An Online Fatigue Damage Evaluation Method for Gas Turbine Hot Components
    Zhu, Hongxin
    Dai, Shun
    Zhang, Xiaoyi
    Chen, Jian
    Luo, Mingyu
    Huang, Weiguang
    ENERGIES, 2023, 16 (19)
  • [29] Temperature Field During the Hot Pressing of Ceramic Gas Turbine Components
    Dutka, Vasily
    Gevorkyan, Edwin
    Rucki, Miroslaw
    Siemiatkowski, Zbigniew
    Morozow, Dmitrij
    Chishkala, Vladimir
    2021 IEEE 8TH INTERNATIONAL WORKSHOP ON METROLOGY FOR AEROSPACE (IEEE METROAEROSPACE), 2021, : 340 - 343
  • [30] Gas turbine hot section components: the challenge of 'residual life' assessment
    Wood, MI
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART A-JOURNAL OF POWER AND ENERGY, 2000, 214 (A3) : 193 - 201
12345