THE FLUORITE-RELATED ANION-EXCESS STRUCTURE OF CEN0.222O0.667F1.333 - ORDERING OF DEFECT CLUSTERS

This investigation presents the preparation of CeN0.222O0.667F1.333 by a solid-state reaction from a mixture of CeN:CeF3:CeO2 = 1:2:1.5 and its structural investigation. The samples were annealed at 900°C in platinum tubes for different times. The basic structure found by powder neutron diffraction is anion-excess fluorite-related. The unit cell is an orthorhombic distortion of the cubic fluorite cell and has the space group Abm2. The lattice constants are a = 577.71(2) pm, b = 572.76(5) pm, and c = 573.32(6) pm. The structure refined by Rietveld analysis shows that [1:0:2]- defect clusters are present. In samples prepared by longer annealing times an ordering of these clusters to larger aggregates, i.e., toward the vernier phases, was observed. This was deduced from full profile analysis without refining a structural model by comparing the instrumental resolution curves of several models. © 1992.