THE MOLECULAR RELAXATION MECHANISMS IN CORK AS STUDIED BY THERMALLY STIMULATED DISCHARGE CURRENTS

被引：17

作者：

MANO, JF ^{[1
]}

CORREIA, NT ^{[1
]}

RAMOS, JJM ^{[1
]}

SARAMAGO, B ^{[1
]}

机构：

[1] Univ Tecn Lisboa, CTR QUIM ESTRUTURAL, INST SUPER TECN, P-1096 LISBON, PORTUGAL

来源：

JOURNAL OF MATERIALS SCIENCE | 1995年 / 30卷 / 08期

关键词：

D O I：

10.1007/BF00353030

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The dielectric relaxation mechanisms present in cork have been investigated in the temperature range - 100 to 100 degrees C using the technique of thermally stimulated discharge currents. A relaxation mechanism was detected which showed a compensation behaviour as observed for the alpha-relaxation (or glass transition relaxation) of synthetic polymers and which lead us to attribute to cork a glass transition-like temperature of 18 degrees C. One lower temperature mechanism was also observed, with low activation enthalpy and entropy, which is presumably originated by local motions (internal rotations) of polar molecular groups. An upper T-g relaxation of higher intensity was also detected which was attributed to large-scale non-cooperative motions of polymeric segments.

引用

页码：2035 / 2041

页数：7

共 21 条

[1]

Pereira H., Wood Sci. Technol., 22, (1988)

[2]

Sittle P., Protoplasma, 54, (1962)

[3]

Pereira H., Rosa M.E., Fortes M.A., Int. Assoc. Wood Anat. Bull., 8, 3, (1987)

[4]

Rosa M.E., Fortes M.A., Mater. Sci. Eng., 100, (1988)

[5]

Rosa M.E., Fortes M.A., J. Mater. Sci., 23, (1988)

[6]

Rosa M.E., Fortes M.A., J. Mater. Sci., 26, (1991)

[7]

Gomes C.M., Fernandes A.C., Almeida B.S., J. Coll. Interface Sci., 156, (1993)

[8]

Veiga I.M., Fernandes A.C., Almeida B.S., Groszek A.J., J. Mater. Sci. Lett., 12, (1993)

[9]

Mourges M., Harmand M.F., Lamure A., Lacabanne C., J. Thermal Anal., 40, (1993)

[10]

Dias A.B., Moura Ramos J.J., Willia G., Polymer, 35, (1994)

← 1 2 3 →