VOLATILIZATION OF TYPE-E BOROSILICATE GLASS

被引:0
作者
HLAVAC, J
KREJCI, J
机构
关键词
D O I
暂无
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The loss in weight due to volatilization of the Eutal alkali-free glass was determined over the temperature range of 1150-1450-degrees-C in a stream of dry and moist nitrogen (p(H2O) = 20 kPa). The volatilization rate is strongly promoted by water vapour pressure. An analysis of the results indicates that the vapour pressure of HBO2 at the melt surface is the decisive factor.
引用
收藏
页码:235 / 243
页数:9
相关论文
共 11 条
[1]  
Cable M., 1975, Glastechnische Berichte, V48, P127
[2]  
HLAVAC J, 1984, SILIKATY, V28, P97
[3]  
HLAVAC J, 1987, SILIKATY, V31, P309
[4]  
HLAVAC J, 1977, 11TH P INT C GLASS P, V1, P229
[5]  
HOLA M, 1974, SILIKATY, V18, P209
[6]  
NEMEC L, 1971, SKLAR KERAMIK, V21, P1
[7]  
Oldfield LF, 1962, GLASS TECHNOL-PART A, V3, P59
[8]  
OLDFIELD LF, 1963, ADV GLASS TECHNOLOGY, P35
[9]  
SEBORSKY J, 1989, SKLAR KERAMIK, V39, P196
[10]  
TATEVOSYAN KM, 1966, STEKLO KERAM