EFFECTS OF HDDR TREATMENT CONDITIONS ON MAGNETIC-PROPERTIES OF ND-FE-B ANISOTROPIC POWDERS

被引:53
作者
NAKAMURA, H
SUEFUJI, R
SUGIMOTO, S
OKADA, M
HOMMA, M
机构
[1] Department of Materials Science, Faculty of Engineering, Tohoku University
关键词
D O I
10.1063/1.358144
中图分类号
O59 [应用物理学];
学科分类号
摘要
It is reported that Nd-Fe-B magnetic powders prepared by utilizing the HDDR (hydrogenation, disproportionation, desorption, and recombination) phenomena exhibit high coercivity, and the addition of Co, Ga, and Zr induces magnetic anisotropy in these powders. HDDR phenomena are caused by the heat treatment in hydrogen (H treatment) and subsequently in vacuum (V treatment). Present works describe the effects of V-treatment conditions on magnetic properties of Nd 12.6Febal.CoxB6.0 (x=0-17.4) alloys. The powders V-treated at lower temperature show lower remanence and no noticeable magnetic anisotropy. V treatment at higher temperature enhances remanence and increases the differences of remanence between the powders aligned with and without magnetic field. Higher values are obtained in Co added alloys. This result suggests that a selective grain growth of Nd2Fe 14B grains during V treatment plays an important role for the inducement of magnetic anisotropy in HDDR-treated powders. The temperature for complete recombination reaction under evacuating condition decreases with increasing Co content. It can be said that Co addition enhances recombination reaction and results in acceleration of grain growth.
引用
收藏
页码:6828 / 6830
页数:3
相关论文
共 7 条
[1]  
HARRIS IR, 1992, 12TH P INT WORKSH RA, P347
[2]   HYDROGENATION, DISPROPORTIONATION AND DESORPTION (HDD) - AN EFFECTIVE PROCESSING ROUTE FOR ND-FE-B-TYPE MAGNETS [J].
MCGUINESS, PJ ;
ZHANG, XJ ;
YIN, XJ ;
HARRIS, IR .
JOURNAL OF THE LESS-COMMON METALS, 1990, 158 (02) :359-365
[3]   HIGH-COERCIVITY SM2FE17NX POWDERS PRODUCED BY HDDR AND NITRIDING PROCESSES [J].
NAKAMURA, H ;
SUGIMOTO, S ;
OKADA, M ;
HOMMA, M .
MATERIALS CHEMISTRY AND PHYSICS, 1992, 32 (03) :280-285
[4]  
TAKESHITA T, 1989, 10TH P INT WORKSH RA, V1, P551
[5]  
TAKESHITA T, 1992, 12TH P INT WORKSH RA, P670
[6]  
TAKESHITA T, 1991, 11TH P INT WORKSH RA, V1, P49
[7]   ORIGIN OF ANISOTROPY IN THE HDDR PROCESS OF ND2FE14B-BASED ALLOYS [J].
UEHARA, M ;
TOMIZAWA, H ;
HIROSAWA, S ;
TOMIDA, T ;
MAEHARA, Y .
IEEE TRANSACTIONS ON MAGNETICS, 1993, 29 (06) :2770-2772