FABRICATION OF 2 TESLA MAGNET USING BI-2212 AG-SHEATHED TAPES

被引：21
作者：
YOSHIDA, M
ENDO, A
HARA, N
机构：
[1] Advanced Technology Research Laboratory, Sumitomo Metal Industries, Amagasaki, Hyogo, 660
来源：
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS | 1994年 / 33卷 / 3B期
关键词：
BI-2212; SUPERCONDUCTING MAGNET; JC; POWDER-IN-TUBE METHOD; AG-SHEATHED TAPE;
D O I：
10.1143/JJAP.33.L421
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Pancake-type superconducting coils were fabricated using Ag-sheathed Bi-2212 tapes. The conventional powder-in-tube method was used where the metal composition of powders are Bi:Sr:Ca:Cu=2:2.3:0.85:2, different from the stoichiometric 2212 composition. Heat treatment was performed in the reduced oxygen partial pressure of 0.01 atm. The superconducting magnet assembled from pancake coils generated a field of 2.0 T at 4.2 K using the 1 X 10(-13) OMEGA.m criterion. The J(c) was 3.9 x 10(4) A/cm2.
引用
收藏
页码：L421 / L423
页数：3
相关论文
共 10 条
  • [1] HIGH CRITICAL CURRENT-DENSITY IN SILVER-SHEATHED BI2SR2CA1CU2AGYOX TAPE
    ASANO, T
    TANAKA, Y
    FUKUTOMI, M
    MAEDA, H
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1990, 29 (07): : L1066 - L1068
  • [2] HOLDER P, 1993, 6TH P INT S SUP HIR
  • [3] PARTIAL MELT GROWTH-PROCESS OF BI2SR2CA1CU2OX TEXTURED TAPES ON SILVER
    KASE, J
    TOGANO, K
    KUMAKURA, H
    DIETDERICH, DR
    IRISAWA, N
    MORIMOTO, T
    MAEDA, H
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1990, 29 (07): : L1096 - L1099
  • [4] INSITU X-RAY-INVESTIGATION OF THE MELTING OF BI-SR-CA-CU-O PHASES
    POLONKA, J
    XU, M
    LI, Q
    GOLDMAN, AI
    FINNEMORE, DK
    [J]. APPLIED PHYSICS LETTERS, 1991, 59 (27) : 3640 - 3642
  • [5] RUBIN LLM, 1977, APPL PHYS LETT, V61, P1977
  • [6] TRANSPORT CRITICAL CURRENT PROPERTIES OF SILVER-SHEATHED BI-BASED SUPERCONDUCTING TAPES AND COILS AT 4.2 K
    SHIBUTA, N
    UEYAMA, M
    MUKAI, H
    SATO, K
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1991, 30 (12B): : L2083 - L2084
  • [7] SHIBUTANI K, 1992, ADV SUPERCONDUCTIVIT, V5, P725
  • [8] SHIMOYAMA J, 1992, ADV SUPERCONDUCTIVIT, V5, P697
  • [9] MICROSTRUCTURES AND JC-B CHARACTERISTICS OF AG-SHEATHED BI-BASED SUPERCONDUCTING WIRES
    UEYAMA, M
    HIKATA, T
    KATO, T
    SATO, K
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1991, 30 (8A): : L1384 - L1386
  • [10] IMPROVEMENT OF J(C) OF AG-SHEATHED BI-2212 TAPES USING MELT-GROWTH TECHNIQUE UNDER REDUCED OXYGEN PARTIAL-PRESSURE
    YOSHIDA, M
    ENDO, A
    [J]. JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1993, 32 (10B): : L1509 - L1512
1