ION STORAGE PROPERTIES OF CEO2 AND MIXED CEO2/SNO2 COATINGS

被引:57
作者
OREL, ZC
OREL, B
机构
[1] National Institute of Chemistry, Ljubljana, 61115
关键词
D O I
10.1007/BF01184574
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Ion storage CeO2 and CeO2/SnO2 coatings were prepared by the sol-gel dip-coating method using an aqueous-based process. The influence of added SnO2 in the CeO2 oxide coatings on the inserted/extracted charge was determined by chronocoulometric measurements. It was found that for 60 nm thick film, the inserted/extracted charge was twice (Q = 10 mC cm(-2)) as large for films containing 17 mol% SnO2, if compared to pure CeO2. The effect of the addition of SnO2 to the mixed oxide coatings on their optical properties and structural characteristics was studied.
引用
收藏
页码:2284 / 2290
页数:7
相关论文
共 18 条
[1]  
[Anonymous], 1978, INFRARED RAMAN SPECT
[2]   MECHANICAL STABILITY OF SOL-GEL FILMS [J].
ATKINSON, A ;
GUPPY, RM .
JOURNAL OF MATERIALS SCIENCE, 1991, 26 (14) :3869-3873
[3]   DIP-COATED TIO2-CEO2 FILMS AS TRANSPARENT COUNTERELECTRODE FOR TRANSMISSIVE ELECTROCHROMIC DEVICES [J].
BAUDRY, P ;
RODRIGUES, ACM ;
AEGERTER, MA ;
BULHOES, LO .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 1990, 121 (1-3) :319-322
[4]   INVESTIGATIONS ON COUNTER ELECTRODE MATERIALS FOR SOLID-STATE ELECTROCHROMIC SYSTEMS [J].
CHU, WF ;
HARTMANN, R ;
LEONHARD, V ;
GANSON, G .
MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1992, 13 (03) :235-237
[5]  
Davydov A.A., 1990, INFRARED SPECTROSCOP
[6]   ELECTRICAL-PROPERTIES OF CERIA-BASED OXIDES AND THEIR APPLICATION TO SOLID OXIDE FUEL-CELLS [J].
EGUCHI, K ;
SETOGUCHI, T ;
INOUE, T ;
ARAI, H .
SOLID STATE IONICS, 1992, 52 (1-3) :165-172
[7]  
Hampel C. A., 1960, GLASS IND, V41, P82
[8]  
Henry M., 1992, CHEM SPECTROSCOPY AP, P153
[9]   PREPARATION AND PROPERTIES OF MONODISPERSED COLLOIDAL PARTICLES OF LANTHANIDE COMPOUNDS .2. CERIUM(IV) [J].
HSU, WP ;
RONNQUIST, L ;
MATIJEVIC, E .
LANGMUIR, 1988, 4 (01) :31-37
[10]  
LAVRENCICSTANGA.U, 1993, SOLAR ENERGY MAT SOL, V31, P171