Spray Pyrolised Prepared CuO-ZnO Nanocomposites Thin Films for Ethanol Sensor

被引：4

作者：

Bari, R. H. ^{[1
]}

Patil, S. B. ^{[1
]}

Bari, A. R. ^{[2
]}

机构：

[1] KRN Commerce & MD Sci Coll, GDM Arts, Dept Phys, Nanomat Res Lab, Jamner 424206, India

[2] Arts Commerce & Sci Coll, Dept Phys, Bodwad 425310, India

来源：

MATERIALS FOCUS | 2014年 / 3卷 / 02期

关键词：

Spray Pyrolysis; CuO-ZnO Nanocomposites; Ethanol Gas Sensing; Quick Response; Fast Recovery;

D O I：

10.1166/mat.2014.1143

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In the present investigation we have prepared ZnO, CuO and CuO-ZnO nanocomposites thin films by spray pyrolysis method onto the heated glass substrate at 250 degrees C. As prepared thin films were studied using XRD, FE-SEM to know crystal structure and surface morphology. Elemental composition was studied using energy dispersive of X-rays (EDAX). The average crystalline size was observed to be less than 32 nm. The gas sensing performance of pure ZnO, CuO and different composition of CuO-ZnO was studied on exposure of different gases for 600 ppm. The film sprayed for composition of CuO-ZnO (sample S4) was observed to be most sensitive (S = 89) to ethanol at 350 degrees C. The sensor shows quick response (5 s) and fast recovery (7 s) time. The results are discussed and interpreted.

引用

页码：119 / 124

页数：6

共 15 条

[11] A catalytic application of Cu2O and CuO films deposited over fiberglass [J].

Ramírez-Ortiza, J ;

Ogura, T ;

Medina-Valtierra, J ;

Acosta-Ortiz, SE ;

Bosch, P ;

de los Reyes, JA ;

Lara, VH .

APPLIED SURFACE SCIENCE, 2001, 174 (3-4) :177-184

[12]

Saito N, 2002, ADV MATER, V14, P418, DOI 10.1002/1521-4095(20020318)14:6<418::AID-ADMA418>3.0.CO

[13]

2-K

[14]

Yamazoe N, 1991, SENSOR ACTUAT B-CHEM, V5, P248

[15] Temperature-programmed reduction and temperature-programmed desorption studies of CuO/ZrO2 catalysts [J].

Zhou, RX ;

Yu, TM ;

Jiang, XY ;

Chen, F ;

Zheng, XM .

APPLIED SURFACE SCIENCE, 1999, 148 (3-4) :263-270

← 1 2 →