Curie Temperature and Tunable Dielectric Properties of Barium Strontium Titanate Thick Films

被引:3
作者
Jeon, Sohyun [1 ]
Kim, Insung [2 ]
Min, Bokki [2 ]
Song, Jaesung [2 ]
Yoon, Jondo [1 ]
机构
[1] Kyungnam Univ, Dept Mat Engn, Masan 631701, South Korea
[2] Korea Electrotechnol Res Inst, Elect & Magnet Devices Grp, Chang Won 641120, South Korea
关键词
BST; Thick films; Curie temperature; Tunability; Dielectric properties;
D O I
10.4191/kcers.2006.43.7.421
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
BaSr) TiO3 thick films were prepared by tape casting method, using BaTiO3 and SrTiO3 powder slurry in order to investigate dielectric properties i.e. dielectric constant, epsilon(r), Curie temperature, T-c. Grain growth within (BaSr) TiO3 thick films was observed with increasing weight ratio of BaTiO3. This observation can be explained by phenomena of substitution of Sr2+ ion for Ba2+ ion in the BaTiO3 system. Also, the Curie temperature in (BaSr) TiO3 thick films was shifted to lower temperature range with increasing SrTiO3. Furthermore, Curie temperature having maximum dielectric constant was in the range of -40 degrees C to 30 degrees C, and hence sharper phase transformation occurred at Curie temperature. There occurred decrease in tunability and k-factor of (Ba0.6Sr0.4)TiO3 calculated from the dielectric constant, epsilon(r) above Curie temperature. In addition, above the 60 degrees C, phase fixation was observed. This means that internal stress relief occurred with increasing 90 degrees domains.
引用
收藏
页码:421 / 426
页数:6
相关论文
共 15 条
[1]  
Cho J.-M., 1999, J KOREAN CERAMIC SOC, V36, P965
[2]  
HALMI M, 1988, ADV CERAM MATER, V3, P32
[3]  
Heo D. S., 2004, J KOR CERAM SOC, V41, P444
[4]  
Jeon S. H., 2006, P KIEEME ANN SUMM C, P311
[5]  
Jochi P. C., 2000, APPL PHYS LETT, V77
[6]  
Kim I. S., 2005, P KIEE ANN SUMM C, P2013
[7]  
Kim I. S., 2005, CARTS EUROPE 2005, P17
[8]  
Kim J. H., 1991, J KOR CERAM SOC, V28, P926
[9]  
Koo D., 1999, KOR ASS CRYST GROWTH, V8, P189
[10]  
Lee S. G., 2001, J KIEEME, V14, P460