THE EARLY STAGES OF PRECIPITATION IN AL-LI ALLOYS

被引:0
作者
LENDVAI, J [1 ]
GUDLADT, HJ [1 ]
机构
[1] SWISS FED INST TECHNOL, INST ANGEW PHYS, CH-8093 ZURICH, SWITZERLAND
来源
ZEITSCHRIFT FUR METALLKUNDE | 1993年 / 84卷 / 04期
关键词
D O I
暂无
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The initial stages of precipitation in supersaturated binary Al - Li solid solution alloys are discussed. Results of experimental investigations referring mostly to ageing at or near room temperature are reviewed and compared with predictions of theoretical treatments. In alloys containing more than about 7 at.% Li a fast continuous ordering (spinodal ordering) takes place before the somewhat slower decomposition. There are indications that the decomposition starts with a homogeneous nucleation in the ordered matrix. In artificially aged samples further precipitation takes place during the subsequent room temperature storage by nucleation within the disordered matrix phase. The ordered nature of the precipitates determines their interaction with dislocations and thereby their effect on the mechanical properties of the precipitation-hardened alloy.
引用
收藏
页码:242 / 247
页数:6
相关论文
共 54 条
[1]   PRECIPITATION HARDENING [J].
ARDELL, AJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (12) :2131-2165
[2]   A NEW METHOD FOR THE DETERMINATION OF THE PRECIPITATE-MATRIX INTERFACIAL ENERGY [J].
BAUMANN, SF ;
WILLIAMS, DB .
SCRIPTA METALLURGICA, 1984, 18 (06) :611-616
[3]   EXPERIMENTAL-OBSERVATIONS ON THE NUCLEATION AND GROWTH OF DELTA' (AL3LI) IN DILUTE AL-LI ALLOYS [J].
BAUMANN, SF ;
WILLIAMS, DB .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (07) :1203-1211
[4]   THE FORMATION OF ORDERED DELTA-'-PHASE IN AL-LI ALLOYS BY DIFFUSE AND SMALL-ANGLE NEUTRON-SCATTERING [J].
BLASCHKO, O ;
GLAS, R ;
WEINZIERL, P .
ACTA METALLURGICA ET MATERIALIA, 1990, 38 (06) :1053-1062
[5]   EXPERIMENTAL (TEM AND STEM) INVESTIGATION AND THEORETICAL APPROACH TO THE FATIGUE-INDUCED DISSOLUTION OF DELTA' PRECIPITATES IN A 2.5 WT-PERCENT AL-LI ALLOY [J].
BRECHET, Y ;
LOUCHET, F ;
MARCHIONNI, C ;
VERGERGAUGRY, JL .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1987, 56 (03) :353-366
[6]   ANNEALING OF VACANCIES AND AGING IN AL-LI ALLOYS [J].
CERESARA, S ;
GIARDA, A ;
SANCHEZ, A .
PHILOSOPHICAL MAGAZINE, 1977, 35 (01) :97-110
[7]   DETERMINATION OF DELTA' COHERENT MISCIBILITY GAP IN AL-LI SYSTEM BY SMALL-ANGLE X-RAY-SCATTERING [J].
COCCO, G ;
FAGHERAZZI, G ;
SCHIFFINI, L .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1977, 10 (AUG1) :325-327
[8]   STRENGTHENING MECHANISMS IN AL-LI ALLOYS CONTAINING COHERENT ORDERED PARTICLES [J].
FURUKAWA, M ;
MIURA, Y ;
NEMOTO, M .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1985, 26 (04) :230-235
[9]   ARRANGEMENT OF DEFORMATION INDUCED DISLOCATIONS IN AGED AL-LI ALLOYS [J].
FURUKAWA, M ;
MIURA, Y ;
NEMOTO, M .
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1985, 26 (04) :225-229
[10]  
GENTZBITTEL M, 1987, J HYS S9, V48, P729