Effect of surface treatment on wear behavior of magnesium alloy AZ31

被引：20
作者：
Fouad, Y. [1 ]
El Batanouny, M. [2 ]
机构：
[1] GUC, Dept Mat Engn, Main Entrance Al Tagamoa Al Khames, New Cairo City, Egypt
[2] German Univ, Dept Design & Prod Engn, Cairo, Egypt
来源：
ALEXANDRIA ENGINEERING JOURNAL | 2011年 / 50卷 / 01期
关键词：
Magnesium alloy AZ31; Wear test; Swaged samples; Shot peening; Surface treatment by ball burnishing;
D O I：
10.1016/j.aej.2011.01.003
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In the present study, wear test has been performed on wrought magnesium alloy AZ31 samples. The test samples were in different conditions as; in the as cast alloy or after undergoing different surface treatment of the wrought alloy. The surface treatments included ball burnishing, swaging and shot peening. The shot peening is done at two main pressure loads; 0.1 and 0.3 bars, while other parameters are held constant. The test results show that the wear worst results were observed in the as cast sample at pressure load 0.3 bars, while the shot peening sample has the worst wear rate among all samples at pressure load of 0.1 bars. On the other hand, the hardness test showed that the swaged sample has the highest hardness value among all samples. (C) 2011 Faculty of Engineering, Alexandria University. Production and hosting by Elsevier B.V. All rights reserved.
引用
收藏
页码：19 / 22
页数：4
相关论文
共 12 条
[1]  
Chang L. L., 2008, MAT SCI ENG A
[2]   Mechanical properties and microstructure of a Mg alloy AZ31 prepared by equal-channel angular pressing [J].
Janecek, M. ;
Popov, M. ;
Krieger, M. G. ;
Hellmig, R. J. ;
Estrin, Y. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 462 (1-2) :116-120
[3]   Microstructure and mechanical properties of Mg-Al-Zn alloy sheets severely deformed by asymmetrical rolling [J].
Kim, W. J. ;
Lee, J. B. ;
Kim, W. Y. ;
Jeong, H. T. ;
Jeong, H. G. .
SCRIPTA MATERIALIA, 2007, 56 (04) :309-312
[4]   Controlling microstructures of AZ31 magnesium alloys by an electromagnetic vibration technique during solidification: From experimental observation to theoretical understanding [J].
Li, Mingjun ;
Tamura, Takuya ;
Miwa, Kenji .
ACTA MATERIALIA, 2007, 55 (14) :4635-4643
[5]   Microstructural effects of AZ31 magnesium alloy on its tensile deformation and failure behaviors [J].
Marya, M ;
Hector, LG ;
Verma, R ;
Tong, W .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 418 (1-2) :341-356
[6]  
Morgenstern C., 2008, INT J FATIGUE
[7]   Corrosion fatigue behavior of extruded magnesium alloy AZ31 in sodium chloride solution [J].
Nan, Z. Y. ;
Ishihara, S. ;
Goshima, T. .
INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (07) :1181-1188
[8]   Microstructures and mechanical properties of modified AZ31-Zr-Sc alloys [J].
Wang, S. C. ;
Chou, C. P. ;
Fann, Y. C. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 485 (1-2) :428-438
[9]   Microstructure and properties of friction stir butt-welded AZ31 magnesium alloy [J].
Wang Xunhong ;
Wang Kuaishe .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 431 (1-2) :114-117
[10]   Crack initiation mechanism of extruded AZ31 magnesium alloy in the very high cycle fatigue regime [J].
Yang, F. ;
Yin, S. M. ;
Li, S. X. ;
Zhang, Z. F. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2) :131-136
12