MECHANOOPTICAL PROPERTIES AND STRUCTURE OF SEGMENTED URETHANE-UREA BLOCK COPOLYMERS

被引：0

作者：

GRISHCHENKO, AY ^{[1
]}

TURKOV, VK ^{[1
]}

LETUNOVSKII, MP ^{[1
]}

TREZVOVA, AV ^{[1
]}

机构：

[1] POLIMERSINTEZ SCI IND ASSOC,VLADIMIR,USSR

来源：

VYSOKOMOLEKULYARNYE SOEDINENIYA SERIYA A | 1992年 / 34卷 / 10期

关键词：

D O I：

暂无

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Mechanooptical properties of segmented urethane-urea block copolymers on the base of THF, propylene oxide, ethylene diamine and rigid 4,4'-diphenylmethane diisocyanate (MDI) block have been studied in films by birefringence method. Very high birefringence being a result of microphase separation of components and formation by MDI rigid blocks of domains with presumable MDI chains orientation being perpendicular to the longest axis was observed. The number of these chains in domains was evaluated. The average MM of a domain is above 7000, their linear dimensions are equal to 3-4 nm. Two regions of relaxations transitions were observed. For T is similar to 170-degrees the decay of the percolational cluster and formation of relatively independent domains consisting of rigid MDI blocks were shown. At T > 250-degrees the <<melting>> of domains proceeding in the narrow temperature range for all samples was observed.

引用

页码：84 / 89

页数：6

共 50 条

[41] High-throughput discovery of structure-mechanical property relationships for segmented poly(urethane-urea)s
Sormana, JL
Meredith, JC
MACROMOLECULES, 2004, 37 (06) : 2186 - 2195
[42] DYNAMIC MECHANICAL PROPERTIES OF POLY(UREA URETHANE) BLOCK COPOLYMERS: INFLUENCE OF SOFT SEGMENT STRUCTURE.
Ferguson, James
Kumar, Mahender
Polimeri (Zagreb), 1986, 7 (06): : 149 - 154
[43] Visible-laser ablation on a nanometer scale using urethane-urea copolymers
Egami, C
Kawata, Y
Aoshima, Y
Takeyama, H
Iwata, F
Sugihara, O
Tsuchimori, M
Watanabe, O
Fujimura, H
Okamoto, N
OPTICS COMMUNICATIONS, 1998, 157 (1-6) : 150 - 154
[44] Visible-laser ablation on a nanometer scale using urethane-urea copolymers
Shizuoka Univ, Shizuoka, Japan
Opt Commun, 1-6 (150-154):
[45] Development of segmented poly(urethane-urea) elastomers and elastic fibers having good performance
Ishihara, H
Yoshihara, N
Kotani, T
JOURNAL OF THE SOCIETY OF RHEOLOGY JAPAN, 2001, 29 (04): : 191 - 199
[46] Structure Property Relationship of Micellar Waterborne Poly(Urethane-Urea): Tunable Mechanical Properties and Controlled Release Profiles with Amphiphilic Triblock Copolymers
Chen, Shu-Yi
Kokalari, Ida
Parnell, Steven R.
Smith, Gregory N.
Zeng, Bing-Hong
Way, Tun-Fun
Chuang, Fu-Sheng
Rwei, Alina Y.
LANGMUIR, 2023, 39 (29) : 10033 - 10046
[47] The preparation and properties for poly(HTBN)urethane-urea/OMMT nanocomposites
Li, Zai-Feng
Sun, Jian
Wang, Sheng-Jun
Li, Jin-Yan
Hao, Jun-Song
Du, Juan
Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2010, 26 (08): : 120 - 123
[48] SURFACE CHARACTERIZATION OF SEGMENTED SILOXANE URETHANE BLOCK-COPOLYMERS
BENRASHID, R
NELSON, GL
LINN, JH
HANLEY, KH
WADE, WR
JOURNAL OF APPLIED POLYMER SCIENCE, 1993, 49 (03) : 523 - 537
[49] Molecular aggregation structure of a segmented poly(urethane-urea) elastomer derived from an amino acid-based diisocyanate
Institute for Materials Chemistry and Engineering, Kyushu University, 744 Motooka, Nishi-ku, Fukuoka
819-0395, Japan
不详
819-0395, Japan
不详
819-0395, Japan
Kobunshi Ronbunshu, 1 (31-36):
[50] EFFECT OF SOLVENT EVAPORATION RATE ON MICROPHASE-SEPARATED STRUCTURE OF SEGMENTED POLY(URETHANE-UREA) PREPARED BY SOLUTION CASTING
IKEDA, Y
TABUCHI, M
SEKIGUCHI, Y
MIYAKE, Y
KOHJIYA, S
MACROMOLECULAR CHEMISTRY AND PHYSICS, 1994, 195 (11) : 3615 - 3628

← 1 2 3 4 5 →