JOSEPHSON CHARACTERISTICS IN A-AXIS ORIENTED YBA2CU3O7-DELTA/PRBA2CU3O7-DELTA'/YBA2CU3O7-DELTA JUNCTIONS

被引:124
作者
HASHIMOTO, T
SAGOI, M
MIZUTANI, Y
YOSHIDA, J
MIZUSHIMA, K
机构
[1] Advanced Research Laboratory, Toshiba Research and Development Center, Saiwai-ku, Kawasaki 210, 1, Komukai Toshiba-cho
关键词
D O I
10.1063/1.107208
中图分类号
O59 [应用物理学];
学科分类号
摘要
A sandwich-type all-oxide Josephson junction consisting of an a-axis oriented YBa2Cu3O7-delta/PrBa2Cu3O7-delta'/YBa2Cu3O7-delta structure has been realized and its Josephson characteristics experimentally investigated. Almost all the fabricated junctions showed the Josephson characteristics, including a resistively shunted junction (RSJ)-like current-voltage characteristic and a Fraunhofer-like magnetic-field dependence of the critical current. The obtained maximum values of the critical-current density j(c) and the I(c)R(n) value were 110 A/cm2 and 80-mu-V, respectively, for a 50-nm-thick PBCO interlayer at 3 K. Besides, the temperature dependencies of the critical current and the normal resistance were measured. I(c) was proportional to exp(- aT1/2), where a is a constant.
引用
收藏
页码:1756 / 1758
页数:3
相关论文
共 10 条
[1]   ALL A-AXIS ORIENTED YBA2CU3O7-Y-PRBA2CU3O7-Z-YBA2CU3O7-Y JOSEPHSON DEVICES OPERATING AT 80-K [J].
BARNER, JB ;
ROGERS, CT ;
INAM, A ;
RAMESH, R ;
BERSEY, S .
APPLIED PHYSICS LETTERS, 1991, 59 (06) :742-744
[2]  
BARONE A, 1982, PHYSICS APPLICATIONS
[3]   BI-EPITAXIAL GRAIN-BOUNDARY JUNCTIONS IN YBA2CU3O7 [J].
CHAR, K ;
COLCLOUGH, MS ;
GARRISON, SM ;
NEWMAN, N ;
ZAHARCHUK, G .
APPLIED PHYSICS LETTERS, 1991, 59 (06) :733-735
[4]   SCALING BEHAVIOR IN ELECTRICAL TRANSPORT ACROSS GRAIN-BOUNDARIES IN YBA2CU3O7-DELTA SUPERCONDUCTORS [J].
GROSS, R ;
CHAUDHARI, P ;
KAWASAKI, M ;
GUPTA, A .
PHYSICAL REVIEW B, 1990, 42 (16) :10735-10737
[5]  
LIKAREV KK, 1979, REV MOD PHYS, V51, P101
[6]   FABRICATION OF THIN-FILM-TYPE JOSEPHSON-JUNCTIONS USING A BI-SR-CA-CU-O/BI-SR-CU-O/BI-SR-CA-CU-O STRUCTURE [J].
MIZUNO, K ;
HIGASHINO, K ;
SETSUNE, K ;
WASA, K .
APPLIED PHYSICS LETTERS, 1990, 56 (15) :1469-1471
[7]   FABRICATION OF HETEROEPITAXIAL YBA2CU3O7-X-PRBA2CU3O7-X-YBA2CU3O7-X JOSEPHSON DEVICES GROWN BY LASER DEPOSITION [J].
ROGERS, CT ;
INAM, A ;
HEGDE, MS ;
DUTTA, B ;
WU, XD ;
VENKATESAN, T .
APPLIED PHYSICS LETTERS, 1989, 55 (19) :2032-2034
[8]   STRUCTURAL FEATURES AND SUPERCONDUCTING PROPERTIES OF AS-GROWN Y-BA-CU-O FILMS [J].
SAGOI, M ;
TERASHIMA, Y ;
KUBO, K ;
MIZUTANI, Y ;
MIURA, T ;
YOSHIDA, J ;
MIZUSHIMA, K .
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 1989, 28 (03) :L444-L447
[9]  
SAGOI M, UNPUB
[10]   SUPERCONDUCTING CHARACTERISTICS OF A PLANAR-TYPE HOBA2CU3O7-X-LA1.5BA1.5CU3O7-Y-HOBA2CU3O7-X JUNCTION [J].
TARUTANI, Y ;
FUKAZAWA, T ;
KABASAWA, U ;
TSUKAMOTO, A ;
HIRATANI, M ;
TAKAGI, K .
APPLIED PHYSICS LETTERS, 1991, 58 (23) :2707-2709