OXIDATION-KINETICS, BREAKAWAY OXIDATION, AND INVERSION PHENOMENON IN 9CR-1MO STEELS

被引：39
作者：
KHANNA, AS
RODRIGUEZ, P
GNANAMOORTHY, JB
机构：
[1] Reactor Research Cent, Kalpakkam, India, Reactor Research Cent, Kalpakkam, India
来源：
OXIDATION OF METALS | 1986年 / 26卷 / 3-4期
关键词：
CHEMICAL REACTIONS - Reaction Kinetics;
D O I：
10.1007/BF00659183
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Oxidation behavior has been studied in air, oxygen, and steam at 1 atm pressure from 500-950 degree C. In air/oxygen, weight gains at 700 degree C were lower than those at 600 degree C, while in steam, weight gains at 800 degree C were lower than those at 700 degree C. This inversion phenomenon was observed for 9Cr-1Mo (high Si), 9Cr-1Mo (low Si), and 9Cr-1Mo-Nb steel. Examination of the oxide scales was carried out using SEM/EDAX, AES/ESCA, and X-ray diffraction techniques.
引用
收藏
页码：171 / 200
页数：30
相关论文
共 13 条
[1]  
EDSTROM JO, 1951, J IRON STEEL I, V185, P450
[2]  
Holmes D.R., 1974, CORROSION STEELS CO2
[3]  
Holmes DR, 1974, P CORR STEELS CO2, P151
[4]   OBSERVATIONS OF METAL OXIDE INTERFACE FOR A FE-CR ALLOY [J].
HOWES, VR .
CORROSION SCIENCE, 1968, 8 (04) :221-&
[5]  
KHANNA AS, 1985, T INDIAN I METALS, V38, P147
[6]  
Rowlands P. C., 1974, CORROSION STEELS CO2, P193
[7]  
SANDERSON J, 1983, FERRITIC STEELS HIGH, P78
[8]   THE BREAKDOWN OF THE PROTECTIVE OXIDE FILM ON TRANSITION METAL ALLOYS [J].
SMELTZER, WW .
ACTA METALLURGICA, 1960, 8 (04) :268-270
[9]  
SMITH KF, 1976, MET SCI, V10, P418
[10]  
Taylor J. W., 1974, CORROSION STEELS CO2, P180
12