PROPERTIES OF ULTRA-FINE GRAIN BINDERLESS CEMENTED CARBIDE RCCFN

被引:190
作者
IMASATO, S
TOKUMOTO, K
KITADA, T
SAKAGUCHI, S
机构
[1] Hard Metals Division, Nippon Tungsten Co. Ltd, 815, 20-31, Shimizu 2-choume, Minamiku Fukuoka
关键词
D O I
10.1016/0263-4368(95)92676-B
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Conventional binderless cemented carbide is known as WC-3% TiC-2% TaC cemented carbide with a mean WC grain diameter of about 2 mu m, which does not include a binder phase. This alloy, however, has no binder phase and therefore low strength. The authors investigated the effects of mean diameter of raw WC powder on mechanical characteristics, and found that the smaller the mean diameter of raw WC powder, the lower the temperature at which sintering is possible and the higher the hardness and strength becomes. An investigation was also made on the effects of grain growth suppression additives on the alloy using 0.6 mu m diameter WC powder, which offers the highest mechanical characteristics, with the objective of enhancing characteristics through finer grains. Hardness increased with additional amounts of Cr3C2 and VC. Strength peaked at a certain additive amount, with superior values of H(R)A = 95.5 and transverse-rupture strength = 1.8 GPa. The microstructure was found to be composed of only very fine and uniform carbides; a mirror surface of 7 nm Rtm was obtained by mirror polishing. These characteristics make it possible for this alloy to be used in various optical applications.
引用
收藏
页码:305 / 312
页数:8
相关论文
共 50 条
  • [11] Research progress of binderless cemented carbide
    Liu, Xiangqing
    Lin, Tao
    Guo, Zhimeng
    Li, Huiqian
    Luo, Ji
    Hao, Junjie
    Fenmo Yejin Jishu/Powder Metallurgy Technology, 2007, 25 (04): : 293 - 296
  • [12] Microstructure and tribological behavior of ultra-fine cemented carbides
    Pan Y.Z.
    Zhao J.
    Zhang J.
    1600, Trans Tech Publications Ltd (693): : 586 - 593
  • [13] Ultra-fine grain reconfigurability using CNTFETs
    O'Connor, I.
    Liu, J.
    Navarro, D.
    Hassoune, I.
    Burignat, S.
    Gaffiot, F.
    2007 14TH IEEE INTERNATIONAL CONFERENCE ON ELECTRONICS, CIRCUITS AND SYSTEMS, VOLS 1-4, 2007, : 194 - 197
  • [14] THE PREPARATION OF ULTRA-FINE GRAIN PHOTOGRAPHIC EMULSIONS
    CRAWFORD, BH
    JOURNAL OF SCIENTIFIC INSTRUMENTS, 1954, 31 (09): : 333 - 336
  • [15] On the corrosion behaviour of ultra-fine grain copper
    Vinogradov, A
    Mimaki, T
    Hashimoto, S
    Valiev, R
    SCRIPTA MATERIALIA, 1999, 41 (03) : 319 - 326
  • [16] Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering
    Liu Xiangqing
    Lin Tao
    Shao Huiping
    Guo Zhimeng
    Luo Ji
    Hao Junjie
    RARE METALS, 2008, 27 (03) : 320 - 323
  • [17] Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering
    LIU Xiangqing LIN Tao Shao Huiping GUO Zhimeng LUO Ji HAO Junjie School of Materials Science and Engineering
    Rare Metals, 2008, (03) : 320 - 323
  • [18] Experimental study on the rheological behavior of ultra-fine cemented backfill
    Deng, Xuejie
    Klein, Bern
    Tong, Libin
    de Wit, Benjamin
    CONSTRUCTION AND BUILDING MATERIALS, 2018, 158 : 985 - 994
  • [19] Investigation on sintering principle of ultra-fine cemented carbide prepared by WC-6Co composite powder
    Zhu, Ertao
    Zhang, Jiuxing
    Guo, Shengda
    Yang, Xinyu
    Yang, Jiangao
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [20] Fatigue Properties of Ultra-Fine Grain Austenitic Stainless Steel and the Effect of Hydrogen
    Kubota, Masanobu
    Macadre, Arnaud
    Mori, Koichi
    Mori, Ryo
    12TH INTERNATIONAL FATIGUE CONGRESS (FATIGUE 2018), 2018, 165