ORIGIN OF DARKENING IN 8 WT-PERCENT YTTRIA-ZIRCONIA PLASMA-SPRAYED THERMAL BARRIER COATINGS

被引:76
作者
INGO, GM
机构
[1] Istituto di Teoria e Struttura Elettronica, C.N.R, Roma, 10–00016, Monterotondo Stazione
关键词
PLASMA SPRAYING; YTTRIA; ZIRCONIA; IMPURITIES; SEGREGATION;
D O I
10.1111/j.1151-2916.1991.tb06891.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The orgins of darkening of 8 wt% Y2O3-ZrO2 air plasma-sprayed (APS) and low-pressure plasma-sprayed (LPPS) thermal barrier coatings (TBC) have been studied using X-ray photoelectron spectroscopy. The change of valence states of zirconium, due to the reduction of ZrO2 to Zr2O3, was responsible for darkening of TBC. Quantification of Zr3+ oxide was related both to the black color of TBC and to the spraying technologies and parameters. Furthermore, impurity (Fe, Al, Si, and Na) segregation and exsolution phenomena were monitored as a function of the air thermal treatment (up to 1473 K) and it was demonstrated not to be the origin of darkening.
引用
收藏
页码:381 / 386
页数:6
相关论文
共 52 条
[1]  
ACKERMANN RJ, 1977, J AM CERAM SOC, V60, P341, DOI 10.1111/j.1151-2916.1977.tb15557.x
[2]  
ACKERMANN RJ, 1975, HIGH TEMP SCI, V7, P304
[3]   STRUCTURE AND IONIC MOBILITY OF ZIRCONIA AT HIGH-TEMPERATURE [J].
ALDEBERT, P ;
TRAVERSE, JP .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1985, 68 (01) :34-40
[4]   CHARACTERIZATION OF IRON OXYGEN-SURFACE REACTIONS BY X-RAY PHOTOELECTRON-SPECTROSCOPY [J].
ALLEN, GC ;
TUCKER, PM ;
WILD, RK .
PHILOSOPHICAL MAGAZINE B-PHYSICS OF CONDENSED MATTER STATISTICAL MECHANICS ELECTRONIC OPTICAL AND MAGNETIC PROPERTIES, 1982, 46 (05) :411-421
[5]  
Apelian D., 1983, International Metals Reviews, V28, P271
[6]   XPS INVESTIGATION OF IMPURITY PHASE SEGREGATION IN 25.5-WT-PERCENT CEO2-2.5Y2O3-72ZRO2 PLASMA-SPRAYED THERMAL BARRIER COATINGS [J].
ARFELLI, M ;
INGO, GM ;
MATTOGNO, G .
SURFACE AND INTERFACE ANALYSIS, 1990, 16 (1-12) :452-456
[7]   AES AND EELS SPECTRA FROM ZR, ZR + O-2 AND ZRO2 - PEAK ENERGY SHIFTS AND INTENSITY VARIATIONS AT VARIOUS STAGES OF OXIDATION IN THE PRESSURE RANGE 10(-6)-10(3) TORR [J].
AXELSSON, KO ;
KECK, KE ;
KASEMO, B .
SURFACE SCIENCE, 1985, 164 (01) :109-126
[8]   SURFACE COMPOSITIONAL CHANGES OF ZRO2 IN H2O, H-2 AND ATOMIC-HYDROGEN, INVESTIGATED BY AES AND EELS [J].
AXELSSON, KO ;
KECK, KE ;
KASEMO, B .
APPLIED SURFACE SCIENCE, 1986, 25 (1-2) :217-230
[9]   CORE AND VALENCE LEVEL PHOTOEMISSION STUDIES OF IRON-OXIDE SURFACES AND OXIDATION OF IRON [J].
BRUNDLE, CR ;
CHUANG, TJ ;
WANDELT, K .
SURFACE SCIENCE, 1977, 68 (01) :459-468
[10]   ELECTRON-ENERGY-LOSS STUDY OF CLEAN AND OXYGEN-EXPOSED POLYCRYSTALLINE ZIRCONIUM [J].
CORALLO, GR ;
ASBURY, DA ;
GILBERT, RE ;
HOFLUND, GB .
PHYSICAL REVIEW B, 1987, 35 (18) :9451-9459