LASER REMELTING OF PLASMA-SPRAYED COATINGS ON COBALT-BASED ALLOYS

被引:5
作者
HWANG, JR
SHAN, YS
DOONG, JL
机构
[1] Department of Mechanical Engineering, National Central University, Chung-Li
关键词
D O I
10.1016/0257-8972(90)90147-5
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Laser remelting of plasma-sprayed coatings can eliminate porosity and develop metallurgical bonding at the coating-substrate interface. In the present study, stellite no. 6 powder was plasma sprayed onto an AISI 1020 carbon steel. Suitable operating conditions for plasma spraying were initially determined. Under such conditions, the effects of laser remelting on the surface roughness, shear bonding strength and wear resistance were studied. The results show that surface roughness is reduced by the remelting process, and little porosity can be found in the remelted regions. The shear bonding strength is apparently increased by the remelting process. The improvement increases with the heat input of laser processing. Wear resistance against high stress abrasion is improved by the remelting process. However, for low stress abrasion, wear resistance is improved only by some remelting processes. The wear resistance increases with laser processing power for both wear tests. © 1990.
引用
收藏
页码:365 / 376
页数:12
相关论文
共 12 条
[1]  
BHAT H, 1983, LASER MAT PROCESSING, P176
[2]   HIGH-POWER LASER-BEAM CLADDING [J].
BRUCK, GJ .
JOURNAL OF METALS, 1987, 39 (02) :10-13
[3]   LASER PROCESSING OF PLASMA-SPRAYED COATINGS [J].
CAPP, ML ;
RIGSBEE, JM .
MATERIALS SCIENCE AND ENGINEERING, 1984, 62 (01) :49-56
[4]  
COQUERELLE G, 1986, 3RD P INT C LAS MAN, P197
[5]   PULSED LASER TREATMENT OF PLASMA SPRAYED COATINGS [J].
DALLAIRE, S ;
CIELO, P .
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1982, 13 (03) :479-483
[6]  
DONALDSON EG, 1986, BR FOUNDRYMAN JUL, P262
[7]  
EBOO GM, 1985, P SOC PHOTO-OPT INST, V527, P86, DOI 10.1117/12.946399
[8]  
HAWKES IC, 1983, 1ST P INT C LAS MAN, P97
[9]   A FUNDAMENTAL-STUDY OF LASER TRANSFORMATION HARDENING [J].
KOU, S ;
SUN, DK ;
LE, YP .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (04) :643-653
[10]  
MORITA T, 1986, 5TH P INT C APPL LAS, P121