Hot Corrosion Behavior of High-Chromium, High-Carbon Cast Irons in NaCl-KCl Molten Salts

被引：8

作者：

Vuelvas-Rayo, S. ^{[1
]}

Gonzalez-Rodriguez, J. G. ^{[1
]}

Porcayo-Calderon, J. ^{[2
]}

Salinas-Bravo, V. M. ^{[2
]}

Maldonado-Ruiz, S. I. ^{[3
]}

机构：

[1] Univ Autonoma Estado Morelos, CIICAp, Ave Univ 1001,Col Chamilpa, Cuernavaca 62500, Morelos, Mexico

[2] IIE, Gerencia Mat & Proc Quimicos, Cuernavaca 62490, Morelos, Mexico

[3] Univ Autonoma Zacatecas, Fac Ingn, Zacatecas 98068, ZAC, Mexico

来源：

INTERNATIONAL JOURNAL OF CORROSION | 2012年 / 2012卷

关键词：

D O I：

10.1155/2012/479761

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

A study on the corrosion behavior of a series of experimental high-chromium (18.53-30.48 wt.%), high-carbon (3.82-5.17%) cast irons in NaCl-KCl (1 : 1M) at 670 degrees C has been evaluated by using weight loss technique and compared with a 304-type stainless steel. It was found that all castings had a higher corrosion rate than conventional 304SS and that the addition of Cr increased the degradation rate of the cast irons. Additionally, corrosion rate increased by increasing the C contents up to 4.29%, but it decreased with a further increase in its contents. Results are discussed in terms of consumption of the Cr2O3 layer by the melt.

引用

页数：9

共 50 条

[31] Wear resistance of high chromium -: high carbon cast irons [J].

Maldonado-Ruíz, SI ;

Velasco, A ;

Colás, R ;

López, D .

INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 15 (06) :589-594

[32] Effect of copper addition on the characteristics of high-carbon and high-chromium steels [J].

Kang, Jun-Yun ;

Heo, Yoon-Uk ;

Kim, Hoyoung ;

Suh, Dong-Woo ;

Son, Dongmin ;

Lee, Dong Hee ;

Lee, Tae-Ho .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 614 :36-44

[33] Simulation of the Phase Diagrams for High-chromium White Cast Irons and Multi-component White Cast Irons [J].

Yen, Chien-Lung ;

Liu, Kun-Lin ;

Pan, Yung-Ning .

ADVANCED RESEARCH ON ENERGY, CHEMISTRY AND MATERIALS APPLICATION, 2014, 848 :39-+

[34] HOW AUSFORMING STRENGTHENS HIGH-CARBON, HIGH-CHROMIUM STEEL. [J].

Das, A.K. ;

Gupte, P.K. .

Metals and Materials, 1974, 8 (11-12) :492-495

[35] Erosion Wear Behavior of High Chromium Cast Irons [J].

Bratislav M. Rajicic ;

A. Maslarevic ;

G. M. Bakic ;

V. Maksimovic ;

M. B. Djukic .

Transactions of the Indian Institute of Metals, 2023, 76 :1427-1437

[36] Erosion Wear Behavior of High Chromium Cast Irons [J].

Rajicic, Bratislav M. ;

Maslarevic, A. ;

Bakic, G. M. ;

Maksimovic, V. ;

Djukic, M. B. .

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2023, 76 (06) :1427-1437

[37] Corrosion behavior and mechanism of 316 stainless steel in NaCl-KCl-ZnCl2 molten salts at high temperature [J].

Hu, Zhe ;

Liu, Linlin ;

Lu, Pengfei ;

Liu, Weihua ;

Zhang, Fan ;

Tang, Zhongfeng .

MATERIALS TODAY COMMUNICATIONS, 2022, 31

[38] Corrosion Mechanism and Properties of 316L Stainless Steel in NaCl-KCl Molten Salt at High Temperatures [J].

Lv, Ruimin ;

Tang, Xian ;

Ying, Zhemian ;

Ai, Hua ;

Sun, Hua ;

Zhang, Wei ;

Wang, Ying ;

Cheng, Jinjuan ;

Yan, Long .

CRYSTALS, 2025, 15 (03)

[39] METALLOGRAPHIC ETCHING FOR CARBIDE VOLUME FRACTION OF HIGH-CHROMIUM WHITE CAST IRONS [J].

COLLINS, WK ;

WATSON, JC .

MATERIALS CHARACTERIZATION, 1990, 24 (04) :379-386

[40] EFFECT OF BORON ON THE PHASE-COMPOSITION OF HIGH-CHROMIUM WHITE CAST IRONS [J].

NARODNITSKII, DB .

METAL SCIENCE AND HEAT TREATMENT, 1979, 21 (7-8) :597-599

← 1 2 3 4 5 →