PURIFICATION OF COPPER BY ANION-EXCHANGE METHOD

被引：1

作者：

ISSHIKI, M

KEKESI, T

MASUMOTO, K

机构：

[1] ISHINOMAKI SENSYU UNIV, FAC SCI & ENGN, DEPT ELECTR MAT, ISHINOMAKI, JAPAN

[2] RES INST ELECT & MAGNET MAT, SENDAI, JAPAN

来源：

JOURNAL OF THE JAPAN INSTITUTE OF METALS | 1992年 / 56卷 / 08期

关键词：

ANION EXCHANGE; HIGH PURITY COPPER; RESIDUAL RESISTIVITY RATIO; ANNEALING IN HYDROGEN; ANNEALING IN VACUUM; COPPER CHLORIDE;

D O I：

10.2320/jinstmet1952.56.8_897

中图分类号：

学科分类号：

摘要：

The anion exchange method in a hydrochloric acid solution was applied for the preparation of high purity copper using CuCl as a starting material. The purified copper chloride solution was evaporated to dryness and reduced by hydrogen. After arc-melting, specimens with the dimensions of 0.5 x 1.0 x 20 mm3 were prepared by cold rolling and subjected to the annealing process which consists of heating in dry hydrogen for 20 h and in vacuum for 20 h at 873 K. The residual resistivity ratio of purified copper was 1470, while that of the copper prepared directly from the starting material and treated in the same way was 36. This result revealed that the anion exchange method is very effective for the preparation of high purity copper.

引用

页码：897 / 899

页数：3

共 6 条

[1] BISHOFF A, 1984, 34TH P EL COMP C IEE, P441
[2] BRUNING H, 1985, ANN CHIM-SCI MAT, V10, P521
[3] FLETCHER AW, 1986, T I MIN METALL C, V95, pC117
[4] PREPARATION OF HIGH-PURITY IRON AND ITS RECRYSTALLIZATION TEMPERATURE
ISSHIKI, M
IGAKI, K
[J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1977, 18 (05): : 412 - 422
[5] PREPARATION OF HIGH-PURITY COBALT
ISSHIKI, M
FUKUDA, Y
IGAKI, K
[J]. JOURNAL OF THE LESS-COMMON METALS, 1985, 105 (02): : 211 - 220
[6] Kraus K. A., 1955, P INT C PEACEFUL USE, V7, P113

← 1 →