IMPEDANCE STUDIES OF THE OXIDE LAYER ON ZIRCALOY AFTER PREVIOUS OXIDATION IN WATER-VAPOR AT 400-DEGREES-C

被引：57

作者：

GOHR, H

SCHALLER, J

SCHILLER, CA

机构：

[1] Institut für Physikalische und Theoretische Chemie, Universität Erlangen-Nürnberg

来源：

ELECTROCHIMICA ACTA | 1993年 / 38卷 / 14期

关键词：

ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY (EIS); HIGH TEMPERATURE; OXIDE LAYER; ZIRCONIUM (ZIRCALOY);

D O I：

10.1016/0013-4686(93)80323-R

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

Zircaloy samples were oxidized in water vapour at 400-degrees-C and 105 bar for up to 90 days. The samples were then studied by EIS in 0.5M K2SO4 at 20-200-degrees-C (1-15 bar). Evaluation yields data about layer thickness, irreversible penetration of electrolyte into pores aided by increasing pressure, activation energies of transport processes from the temperature dependence of kinetic parameters.

引用

页码：1961 / 1964

页数：4

共 16 条

[1] Dispersion and absorption in dielectrics I. Alternating current characteristics
Cole, KS
Cole, RH
[J]. JOURNAL OF CHEMICAL PHYSICS, 1941, 9 (04) : 341 - 351
[2] GOHR H, 1981, BER BUNSEN PHYS CHEM, V85, P274
[3] GOHR H, 1981, DECHEMA MONOGR, V90, P1
[4] GOHR H, 1983, 34TH M INT SOC EL ER, P621
[5] KASPAR K, SIEMENS UB KWU BT 61
[6] KASS S, 1963, CORROSION ZIRCONIUM, P3
[7] REVIEW OF MECHANISTIC ANALYSIS BY ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY
MACDONALD, DD
[J]. ELECTROCHIMICA ACTA, 1990, 35 (10) : 1509 - 1525
[8] Mandelbrot B. B., 1982, FRACTAL GEOMETRY NAT, P1
[9] MEISSNER W, 1974, METHODE MESSUNG AUSW
[10] MULLER N, 1980, THESIS ERLANGEN

← 1 2 →