HYDROGEN INDUCED SLOW CRACK-GROWTH IN STABLE AUSTENITIC STAINLESS-STEELS

被引:76
作者
CHU, WY
YAO, J
HSIAO, CM
机构
来源
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1984年 / 15卷 / 04期
关键词
D O I
10.1007/BF02644204
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
引用
收藏
页码:729 / 733
页数:5
相关论文
共 15 条
[1]   HYDROGEN ASSISTED CRACKING OF TYPE-304 STAINLESS-STEEL [J].
BRIANT, CL .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (02) :181-189
[2]  
Brown B.F., 1972, STRESS CORROSION CRA, P1
[3]   MECHANISM OF STRESS-CORROSION CRACKING OF LOW-ALLOY STEEL IN WATER [J].
CHU, WY ;
LIU, TH ;
HSIAO, CM ;
LI, SQ .
CORROSION, 1981, 37 (06) :320-327
[4]   MECHANISM OF STRESS-CORROSION CRACKING OF STEELS IN H2S [J].
CHU, WY ;
LI, SQ ;
HAIAO, CM ;
TIEN, JZ .
CORROSION, 1980, 36 (09) :475-482
[5]   NEW ENGINEERING FRACTURE-TOUGHNESS PARAMETER-KISCC(RHO) [J].
CHU, WY ;
HSIAO, CM ;
LI, SQ .
SCRIPTA METALLURGICA, 1979, 13 (11) :1057-1062
[6]   RESEARCH OF HYDROGEN INDUCED CRACKING AND STRESS-CORROSION CRACKING IN AN ALUMINUM-ALLOY [J].
CHU, WY ;
WANG, YB ;
HSIAO, CM .
CORROSION, 1982, 38 (11) :561-570
[7]   EFFECT OF HYDROGEN ON THE APPARENT YIELD STRESS - RESEARCH ON THE CAUSE OF HYDROGEN INDUCED DELAYED PLASTICITY [J].
CHU, WY ;
LI, SQ ;
HSIAO, CM ;
JU, SY .
CORROSION, 1981, 37 (09) :514-521
[8]   INFLUENCE OF AUSTENITE STABILITY ON THE HYDROGEN EMBRITTLEMENT AND STRESS-CORROSION CRACKING OF STAINLESS-STEEL [J].
ELIEZER, D ;
CHAKRAPANI, DG ;
ALTSTETTER, CJ ;
PUGH, EN .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (07) :935-941
[9]  
KOLTS J, 1976, ASTM STP, V610, P336
[10]   ROLE OF HYDROGEN IN STRESS-CORROSION CRACKING OF AUSTENITIC STAINLESS-STEELS [J].
MEHTA, ML ;
BURKE, J .
CORROSION, 1975, 31 (03) :108-110