HYGROTHERMAL INFLUENCE ON DELAMINATION BEHAVIOR OF GRAPHITE EPOXY LAMINATES

被引：48

作者：

GARG, A ^{[1
]}

ISHAI, O ^{[1
]}

机构：

[1] NASA,AMES RES CTR,MOFFETT FIELD,CA 94035

来源：

ENGINEERING FRACTURE MECHANICS | 1985年 / 22卷 / 03期

关键词：

LAMINATED PRODUCTS - Moisture Control - MATERIALS TESTING - Thermal Effects;

D O I：

10.1016/0013-7944(85)90142-0

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

The hygrothermal effect on the fracture behavior of graphite/epoxy laminates has been investigated as part of an overall effort to develop a methodology for damage-tolerance predictions in advanced composite materials. Several T300/934 laminates were tested using a number of specimen configurations (double cantilever, compact tension, and cracked lap shear) in order to evaluate the effects of temperature and humidity on delamination fracture toughness under Mode I and Mode II loading. The specimens were exposed to different humidity levels and temperatures for varying periods of time prior to testing. The preexposed specimens were tested under room conditions, and fracture energies during initiation and propagation were estimated. Acoustic emission was used to detect crack initiation.

引用

页码：413 / 427

页数：15

共 29 条

[1]

BASCOM WD, 1980, COMPOSITES, V10, P9

[2]

BASCOM WD, 1980, ADHESION, V6, P185

[3]

CHARENTENAY FX, 1979, ICM 3 CAMBRIDGE, V3, P241

[4]

Crossman F. W., 1982, ASTM STP, P118

[5]

CULLEN JS, 1981, THESIS TEXAS A M U C

[6]

DEVITT DF, 1980, J COMPOS MATER, V14, P270

[7] FRACTURE MECHANICS OF COMPOSITE-MATERIALS [J].

DHARAN, CKH .

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1978, 100 (03) :233-247

[8]

Hamstad MA, 1982, AMMRC MS 82 3, P221

[9] THE INTERLAMINAR FRACTURE ENERGY OF GLASS-FIBER REINFORCED POLYESTER COMPOSITES [J].

HAN, KS ;

KOUTSKY, J .

JOURNAL OF COMPOSITE MATERIALS, 1981, 15 (JUL) :371-388

[10]

HAN KS, 1983, COMPOSITES, V13, P67

← 1 2 3 →